Starex WR-9700 T

Identification & Functionality

Chemical Family

Styrenics

Polymer Name

Acrylonitrile Styrene Acrylate (ASA)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Applications & Uses

Markets

Building & Construction

Applications

Building & Construction — Building Materials

Pipes & Plumbing

Plastics & Elastomers End Uses

Fittings

Plastics & Elastomers Processing Methods

Extrusion

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength at Yield (50 mm/min)	47	MPa	ISO 527
Tensile Strength at Break (50 mm/min)	35	MPa	ISO 527
Rockwell Hardness	109	Scale R	ASTM D 785
Tensile Modulus (50 mm/min)	2200	MPa	ASTM D 638
Tensile Strain at Break (50 mm/min)	15	%	ISO 527
Flexural Strength (2 mm/min)	67	MPa	ISO 178
Flexural Modulus (2 mm/min)	1860	MPa	ISO 178
Charpy Impact Strength - V-notched (23°C, 4mm)	10	kJ/m2	ISO 179 1eA
Notched Izod Impact Strength (23°C, 4 mm)	7	kJ/m2	ISO 180 1A

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity (Natural or representative color)	1.07	-	ISO 1183
Melt Flow Index - MFI (220°C/10 kg)	11	g/10 min	ISO 1133
Molding Shrinkage - MD (Flow at 2mm)	0.40~0.70	%	ISO 294-4
Molding Shrinkage - TD (Cross-Flow at 2mm)	0.40~0.70	%	ISO 294-4

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm)	92	°C	ISO 75-2
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm)	80	°C	ISO 75-2