Starex WX-9310UV

Identification & Functionality

Chemical Family

Styrenics

Polymer Name

Acrylonitrile Styrene Acrylate (ASA)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Materials Features

Heat Resistance

Applications & Uses

Markets

Automotive & Transportation

Applications

Automotive & Transportation — Automotive

Exterior & Body,

Interior,

Other Automotive Applications

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Exterior Parts,

Automotive Interior Parts

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength at Yield (50 mm/min)	49	MPa	ISO 527
Tensile Strength at Break (50 mm/min)	37	MPa	ISO 527
Rockwell Hardness	106	Scale R	ASTM D785
Tensile Modulus (50 mm/min)	2200	MPa	ASTM D 638
Tensile Strain at Break (50 mm/min)	12	%	ISO 527
Flexural Strength (2 mm/min)	70	MPa	ISO 178
Flexural Modulus (2 mm/min)	2400	MPa	ISO 178
Charpy Impact Strength - V-notched (23°C, 4mm)	14	kJ/m2	ISO 179 1eA
Notched Izod Impact Strength (23°C, 4 mm)	16	kJ/m2	ISO 180 1A

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity (Natural or representative color)	1.08	-	ISO 1183
Melt Flow Index - MFI (220°C/10 kg)	6	g/10 min	ISO 1133
Molding Shrinkage - MD (Flow at 2mm)	0.4 - 0.7	%	ISO 294-4
Molding Shrinkage - TD (Cross-Flow at 2mm)	0.4 - 0.7	%	ISO 294-4

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (0.45 MPa, Annealed, 4 mm)	106	°C	ISO 75-2
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm)	96	°C	ISO 75-2
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm)	80	°C	ISO 75-2
Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm)	102	°C	ISO 75-2

Regulatory & Compliance

Certifications & Compliance

Kosher