- Good processability in existing LDPE machines
- Suitable as sealant layer for flexible packaging
- Suitable to blown film applications, i.e. bags etc.
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Process Information
Recommended processing conditions Blown film Cast film Temperature 140-150°C 150-170°C Die lip gap 0.8-1.5 mm 0.5-1.0 mm Others B.U.R.: 2-4 Roll temp.: 25-35 °C
*The conditions are one example for film fabrication.
Please consult with us before your trial and production.
Properties
- Color
- Typical Properties
Value | Units | Test Method / Conditions | |
Melt Flow Rate (at 160°C, 21.2 N) | 5.0 | g/10 min | ISO 1133 |
Density | 1.29 | g/cm3 | ISO 1183 |
Young Modulus (MD) | 510.0 | MPa | ISO 527-3 |
Young Modulus (TD) | 510.0 | MPa | ISO 527-3 |
Yield Stress (MD) | 16.0 | MPa | ISO 527-3 |
Yield Stress (TD) | 16.0 | MPa | ISO 527-3 |
Tensile Strength (MD) | 41.0 | MPa | ISO 527-3 |
Elongation at Beak (MD) | 730.0 | % | ISO 527-3 |
Elmendorf Tear Strength (MD) | 3.0 | N/mm | ISO 6383-2 |
Puncture Impact Strength | 17000.0 | J/m | MCC method |
Bio-based Content (Calculated) | 40.0 | % | ASTM D6866 |
Thickness | 31.0 | μm | — |
Haze | 76.0 | — | ISO 14782 |
Gloss | 15.0 | — | JIS Z 8741 |
Elmendorf Tear Strength (TD) | 15.0 | N/mm | ISO 6383-2 |
Elongation at Beak (TD) | 850.0 | % | ISO 527-3 |
Tensile Strength (TD) | 40.0 | MPa | ISO 527-3 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage Condition
FORZEAS™ pellets are dried and packed in aluminum-lined packaging before delivering to customers. Do not store outdoors. Keep dry at ambient temperature. Avoid humid environment, heat and direct sunlight. Use material as soon as possible after the delivery, in order to prevent possible material quality deterioration. Pre-dry of the unopened FORZEAS™ is not necessary. It is recommended to keep packages sealed until ready to process and using up the whole 25-kg bag. Unused material should be tightly sealed, kept away from open air, and pre-dried (at 60 °C for over 5 hours).