- DIN 18820-1
- Clear unaccelerated
- High reactivity
- Fast curing
- Type 1140 (DIN 16946-2)
Applications & Uses
- Markets
- Applications
Properties
- Color
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Solid Content | 59 - 63 | % | MT-CU001C |
Brookfield Viscosity at 25°C, sp 2 rpm 20 | 280 - 370 | mPa.s | MT-CU025V |
Peak at 25°C + 0,5% Co 1% + 2% MEKP50 | 8-12 | — | RS.03.G minutes |
Exothermic peak at 25°C + 0,5% Co 1% + 2% MEKP50 | 180 - 205 | °C | RS.03.G |
Specific weight at 20°C | 1,11 | g/cm3 | — |
Value | Units | Test Method / Conditions | |
Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 130 | MPa | ISO 178/B (2010) |
Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 105 | °C | ASTM E 1545 (2011) |
Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 48 | — | ASTM D 2583 (2007) |
Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 75 | MPa | ISO 527 (2012) |
Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3700 | MPa | ISO 527 (2012) |
Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3700 | MPa | ISO 178/B (2010) |
HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 92 | °C | ISO 75 -2A (2013) |
Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2,7 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature