Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Low viscosity
- Clear unaccelerated
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 54 - 58 | % | MT-CU001C |
| Specific weight at 20°C | 1,09 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 110 - 150 | mPa.s | MT-CU025V |
| Gel Time on 50 g resin at 20°C + 0,3% Co 6% + 1,5% MEKP50 | 9-12 | minutes | RS.08.G |
| Delta at 20°C + 0,3% Co 6% + 1,5% MEKP50 | 11-19 | minutes | RS.08.G |
| Exothermic peak at 20°C + 0,3% Co 6% + 1,5% MEKP50 | 110 - 140 | °C | RS.08.G |
| Value | Units | Test Method / Conditions | |
| Curing Cycle at 23°C (at 100°C) | 24 (2) | hr | — |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3800 | MPa | ISO 178/B (2010) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 44 | — | ASTM D 2583 (2007) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 75 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3800 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 120 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 65 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 80 | °C | ASTM E 1545 (2011) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2,3 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature