Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Preaccelerated
- Without styrene in a reactive monomer
- Thixotropic
- Very good chemical resistance
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1.05 - 1.10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 800 - 1000 | mPa.s | MT-CUT23V |
| Solid Content | 50 - 55 | % | MT-CU001C |
| Gel Time | 15 - 23 | minutes | MT-CU149R |
| Curing Time | 20 - 30 | minutes | MT-CU149R |
| Exothermic peak | 130 - 140 | °C | MT-CU149R |
| Value | Units | Test Method / Conditions | |
| Flexural strength | 70 | MPa | ISO 178 (2011) |
| Flexural modulus | 3500 | MPa | ISO 178 (2011) |
| Curing Cycle at 80°C (at 120°C) | 16 (2) | hr | — |
| Tensile strength | 30 | MPa | ISO 527 (1999) |
| Tensile Modulus | 3500 | MPa | ISO 527 (2012) |
| Elongation at break | 0.8 | % | ISO 527 (2012) |
| HDT | 118 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C | 55 | — | ASTM D 2583 (2007) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature