Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Fire retardand properties
- Medium reactivity
- Very good chemical resistance
- Medium viscosity
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 62 - 66 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 250 - 450 | mPa.s | MT-CU023V |
| Specific weight at 20°C | 1.10 - 1.20 | g/cm3 | — |
| Gel Time | 15 - 25 | minutes | MT-CU200R |
| Exothermic peak | 150 - 170 | °C | MT-CU200R |
| Peak (23°C) | 30 - 50 | — | — |
| Value | Units | Test Method / Conditions | |
| Curing Cycle at 23°C (at 100°C) | 24 (2) | hr | — |
| Flexural modulus | 3500 | MPa | ISO 178 (2011) |
| Tensile strength | 90 | MPa | ISO 527 (2012) |
| Tensile Modulus | 4200 | MPa | ISO 527 (2012) |
| Elongation at break | 3.6 | % | ISO 527 (2012) |
| Flexural strength | 140 | MPa | ISO 178 (2011) |
| HDT | 117 | °C | ISO 75 -2A (2013) |
Storage & Handling
- Shelf Life
- 12 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature