Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Preaccelerated
- Thixotropic
- High hydrolisys resistance
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 60 - 64 | % | MT-CU001C |
| Specific weight at 20°C | 1.00 - 1.10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 450 - 550 | mPa.s | MT-CUT25V |
| Gel Time | 27 - 33 | minutes | MT-CU202R |
| Exothermic peak | 125 - 145 | °C | MT-CU202R |
| Peak (23°C) | 40 - 50 | — | — |
| Value | Units | Test Method / Conditions | |
| Curing Cycle at 23°C (at 100°C) | 24 (2) | hr | — |
| Flexural strength | 65 | MPa | ISO 178 (2011) |
| Tensile strength | 40 | MPa | ISO 527 (2012) |
| Tensile Modulus | 3400 | MPa | ISO 527 (2012) |
| Elongation at break | 1.35 | % | ISO 527 (2012) |
| Flexural modulus | 3460 | MPa | ISO 178 (2011) |
| HDT | 93 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature