Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Thickenable with MgO
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 58 - 62 | % | MT-CU001C |
| Specific weight at 20°C | 1.05 - 1.10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 4 rpm 50 | 20 - 24 | mPa.s | MT-CU023V |
| Peak at 130°C + 1% TBPB | 8-10 | minutes | MT-CU161R |
| Exothermic peak at 130°C + 1% TBPB | 135 - 155 | °C | MT-CU161R |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 80°C for 4h /+2 at 120°C | 35 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 4h /+2 at 120°C | 3500 | MPa | ISO 527 (2012) |
| Elongation at break at 80°C for 4h /+2 at 120°C | 1.25 | % | ISO 527 (2012) |
| Flexural strength at 80°C for 4h /+2 at 120°C | 80 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 4h /+2 at 120°C | 3000 | MPa | ISO 178 (2011) |
| HDT at 80°C for 4h /+2 at 120°C | 130 | °C | ISO 75 -2A (2013) |
| Glass transition at 80°C for 4h /+2 at 120°C | 158 | °C | ASTM E 1545 (2011) |
Storage & Handling
- Shelf Life
- 12 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature