Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Thickenable with MgO
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Gel Time at 130°C + 1% TBPB | 55 - 75 | sec | MT-CU003R |
| Exothermic peak at 130°C + 1% TBPB | 260 - 280 | °C | MT-CU003R |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 1500 - 1700 | mPa.s | MT-CU023V |
| Solid Content | 65 - 68 | % | MT-CU001C |
| Delta at 130°C + 1% TBPB | 1:20 - 2:00 | minutes | MT-CU003R |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 80°C for 16h / +2h at 140°C | 1,4 | % | ISO 527 (2012) |
| Curing Cycle at 80°C (140°C) | 16 (+2) | hr | — |
| Tensile Modulus at 80°C for 16h / +2h at 140°C | 3710 | MPa | ISO 527 (2012) |
| Flexural strength at 80°C for 16h / +2h at 140°C | 113 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16h / +2h at 140°C | 3385 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16h / +2h at 140°C | 127 | °C | ISO 75 -2A (2013) |
| Tensile strength at 80°C for 16h / +2h at 140°C | 43,1 | MPa | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 9 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature