SILIMOLD AD 10 silicon rubber is especially designed for complex molds, model prototype and mold making. Pad printing.
Properties
- Physical Form
- Appearance
- Thick liquid before Catalysis
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Appareance (After Catalysis) | Flexible rubber | — | — |
| Specific Gravity (Comp. A e B, Before Catalysis) | 1.17 - 1.21 | kg/l | — |
| Color (After Catalysis) | Semi bright blue | — | — |
| Color Component A (Before Catalysis) | White | — | — |
| Color Component B (Before Catalysis) | Blue | — | — |
| Demoulding Time (During Catalysis) | 2 | Hrs | — |
| Elongation At Break (After Catalysis) | 570 - 630 | % | DIN 53504 - S A 3 |
| Hardness (After Catalysis) | 10 | Shore A | DIN 53505 |
| Linear Shrinkage (After Catalysis) after 5 days ageing | max. 0.1 | % | ISO 4823 |
| Mixing Ratio (Before Catalysis) by weight (= 10%) | 100 : 10 | — | — |
| Pot Life (During Catalysis) | 5 - 10 | min | — |
| Tearing Strength (After Catalysis) | 17.5 - 20.5 | N/Mm | ASTM D 624 S A 3 |
| Tensile Strength (After Catalysis) | 2.5 - 3.5 | N/mm2 | DIN 53504 - S A 3 |
| Viscosity Comp. A (Before Catalysis) | 4.95 - 5.05 | Cps | — |
| Viscosity Comp. B (Before Catalysis) | 1.95 - 2.05 | Cps | — |
Packaging & Availability
- Packaging Type
- Packing
- Component A: 5 Kg. – 25 Kg. Plastic bucket
- Component B: 0,5 Kg. – 2,5 Kg. Plastic bottle
Storage & Handling
- Shelf Life
Both components (A and B) 12 months in their original tightly closed containers, in a dry and cool place , away from moisture and at temperature between +10°C and +28°C.