Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Wire Coating Extrusion
- Note
¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 28 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 28 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 90 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 840 | MPa | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 720 | MPa | ASTM D790 |
| Hardness (Shore D, 10S reading) ¹¹ | 63 | — | ASTM D2240 |
| Tensile Stress (Yield) ¹¹ | 25 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 25 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 20 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 50 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 690 | MPa | ISO 527 |
| Flexural Modulus ¹¹ | 790 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.03 | — | ASTM D792 |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 33 | g/10 min | ASTM D1238 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 82 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 56 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 66 | °C | ISO 75/Af |
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (1 GHz) ¹¹ | 2.47 | — | ASTM D150 |
| Dissipation Factor (at at 1 GHz) ¹¹ | 0.0032 | — | ASTM D150 |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 560 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 170 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 37 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 14 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Compression Ratio | 2:1-3:1 | — | — |
| Conductor Pre-heat Temperature | 100 - 150 | °C | — |
| Cooling Water Air Gap | 100 - 1000 | mm | — |
| Cross-head Temperature | 280 - 300 | °C | — |
| Die Temperature | 280 - 300 | °C | — |
| Drying Temperature | 80 - 100 | °C | — |
| Drying Time | 4 - 6 | Hrs | — |
| Drying Time (Cumulative) | 8 | Hrs | — |
| Extruder Length/Diameter Ratio (L/D) | min. 24:1 | — | — |
| Feed Zone Temperature | 200 - 260 | °C | — |
| Head Zone Temperature | 280 - 300 | °C | — |
| Maximum Moisture Content | 0.02 | % | — |
| Melt Temperature | 280 - 300 | °C | — |
| Middle Zone Temperatures | 270 - 300 | °C | — |
| Neck Temperature | 280 - 300 | °C | — |
| Screen Pack | 60/200/60 | — | — |
| Screw Speed | 5 - 60 | rpm | — |
| Water Bath Temperature | 15 - 30 | °C | — |