Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Wire Coating Extrusion
- Note
¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 43 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 41 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 15 | % | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 83 | % | ASTM D638 |
Tensile Modulus (at 50 mm/min) ¹¹ | 1710 | MPa | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 53 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 1550 | MPa | ASTM D790 |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 44 | MPa | ISO 527 |
Tensile Stress (Break, 50 mm/min) ¹¹ | 42 | MPa | ISO 527 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 11 | % | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 46 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 1750 | MPa | ISO 527 |
Flexural Stress (Yield, at 2 mm/min) ¹¹ | 59 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 1740 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.03 | — | ASTM D792 |
Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 13.8 | g/10 min | ASTM D1238 |
Density ¹¹ | 1.03 | g/cm³ | ISO 1183 |
Water Absorption (at 23°C, saturated) ¹¹ | 0.12 | % | ISO 62-1 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.05 | % | ISO 62 |
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 13 | cm³/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (Rate B/50) ¹¹ | 114 | °C | ASTM D1525 |
Vicat Softening Temperature (Rate B/50) ¹¹ | 114 | °C | ISO 306 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 92 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000084 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000085 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000111 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000105 | 1/°C | ASTM E831 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 117 | °C | ISO 306 |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 98 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹¹ | 309 | J/m | ASTM D256 |
Izod Impact (Notched, at -30°C) ¹¹ | 67 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 45 | J | ASTM D3763 |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 36 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 33 | kJ/m² | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Conductor Pre-heat Temperature | 80 - 150 | °C | — |
Cooling Water Air Gap | 100 - 200 | mm | — |
Cross-head Temperature | 250 - 285 | °C | — |
Die Temperature | 250 - 285 | °C | — |
Drying Temperature | 60 - 80 | °C | — |
Drying Time | 4 - 6 | Hrs | — |
Drying Time (Cumulative) | 12 | Hrs | — |
Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | — | — |
Feed Zone Temperature | 210 - 260 | °C | — |
Head Zone Temperature | 250 - 285 | °C | — |
Maximum Moisture Content | 0.02 | % | — |
Melt Temperature | 250 - 285 | °C | — |
Middle Zone Temperatures | 230 - 285 | °C | — |
Neck Temperature | 250 - 285 | °C | — |
Screen Pack | 150 - 100 | — | — |
Screw Speed | 15 - 40 | rpm | — |
Water Bath Temperature | 15 - 80 | °C | — |