Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 63 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 61 | MPa | ASTM D638 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 6 | % | ISO 527 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 50 | % | ISO 527 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2350 | MPa | ISO 527 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 95 | % | ASTM D638 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 90 | MPa | ISO 178 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2300 | MPa | ASTM D638 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2300 | MPa | ISO 178 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 95 | MPa | ASTM D790 |
| Ball Indentation Hardness (H358/30) ¹¹ | 95 | MPa | ISO 2039-1 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2390 | MPa | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Mold Shrinkage (on Tensile Bar, flow) ʰ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Density ¹¹ | 1.2 | g/cm³ | ISO 1183 |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 10.2 | g/10 min | ASTM D1238 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.15 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 126 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 150 | °C | ISO 306 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 141 | °C | ISO 306 |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 120 | °C | UL 746B |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 142 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 136 | °C | ISO 75/Be |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 125 | °C | ISO 75/Ae |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 3) ¹¹ | min. 3 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 3 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 7 | PLC Code | ASTM D495 |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 160 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 59 | J | ASTM D3763 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 120 | °C | — |
| Drying Time ⁷ | 3 - 4 | Hrs | — |
| Drying Time ⁷ | 2 - 4 | Hrs | — |
| Drying Time (Cumulative) ⁷ | 48 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.02 | % | — |
| Melt Temperature ⁷ | 295 - 315 | °C | — |
| Melt Temperature ⁷ | 280 - 300 | °C | — |
| Nozzle Temperature ⁷ | 290 - 310 | °C | — |
| Nozzle Temperature ⁷ | 270 - 290 | °C | — |
| Front - Zone 3 Temperature ⁷ | 295 - 315 | °C | — |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 280 - 305 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 270 - 295 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C | — |
| Hopper Temperature ⁷ | 60 - 80 | °C | — |
| Mold Temperature ⁷ | 70 - 95 | °C | — |
| Mold Temperature ⁷ | 80 - 100 | °C | — |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
| Screw Speed ⁷ | 40 - 70 | rpm | — |
| Shot to Cylinder Size ⁷ | 40 - 60 | % | — |
| Vent Depth ⁷ | 0.025 - 0.076 | mm | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |
| UL Recognized (94V-2 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability