- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 22 | MPa | ISO 527 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 20 | % | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | min. 50 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 390 | MPa | ISO 527 |
Hardness (Shore D) ¹¹ | 61 | — | ISO 868 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.01 | g/cm³ | ISO 1183 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 1.1 | % | ISO 62 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.7 | % | ISO 62-1 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.2 | % | ISO 294 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.5 | % | ISO 294 |
Value | Units | Test Method / Conditions | |
Melting Temperature ¹¹ | 172 | °C | ISO 11357-3 |
Vicat Softening Temperature (Rate B/50) ¹¹ | 164 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 120 | kJ/m² | ISO 179/1eA |
Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 20 | kJ/m² | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Melt Temperature ⁷ | 260 | °C | — |
Mold Temperature ⁷ | 164 | °C | — |