Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 100 | % | ASTM D638 |
Tensile Stress (Yield, 5 mm/min) ¹¹ | 62 | MPa | ISO 527 |
Tensile Strain (Yield, 5 mm/min) ¹¹ | 4.5 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 2390 | MPa | ISO 527 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.06 | — | ASTM D792 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 55 | °C | ASTM D648 |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 135 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 62 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | ASTM D257 |
Surface Resistivity ¹¹ | 1.00E+12 | Ω | ASTM D257 |
Relative Permittivity (100 Hz) ¹¹ | 3.6 | — | ASTM D150 |
Relative Permittivity (1 MHz) ¹¹ | 3.2 | — | ASTM D150 |
Dissipation Factor (at 100 Hz) ¹¹ | 0.02 | — | ASTM D150 |
Dissipation Factor (at at 1 kHz) ¹¹ | 0.02 | — | ASTM D150 |
Dissipation Factor (at 100 kHz) ¹¹ | 0.014 | — | ASTM D150 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 80 | °C | — |
Drying Time ⁷ | 4 | Hrs | — |
Maximum Moisture Content ⁷ | 0.12 - 0.2 | % | — |
Melt Temperature ⁷ | 270 - 275 | °C | — |
Front - Zone 3 Temperature ⁷ | 270 - 280 | °C | — |
Middle - Zone 2 Temperature ⁷ | 260 - 270 | °C | — |
Rear - Zone 1 Temperature ⁷ | 255 - 265 | °C | — |
Mold Temperature ⁷ | 65 - 95 | °C | — |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | — |
Screw Speed ⁷ | 30 - 60 | rpm | — |
Value | Units | Test Method / Conditions | |
Oxygen Index (LOI) | 27 | % | ISO 4589 |