LNP™ COLORCOMP™ Compound M1000S

Identification & Functionality

Additives Included

Heat Stabilizer,

Metal Deactivator,

Mold Release Agent

Chemical Family

Polyolefins,

Polypropylenes (PP)

Polymer Name

Polypropylene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Excellent Aesthetics,

Good Aesthetics,

Good Mold Release,

Good Surface Appearance,

Heat Stabilized,

High Durability,

No Added PFAS,

Unreinforced

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Consumer Goods — Housewares

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Interior Parts,

Commercial Appliance,

Consumer Applications,

Containers,

Home Appliances,

Home Decors,

Household Goods,

Personal Accessories,

Sporting Goods

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Custom

Physical Properties

	Value	Units	Test Method / Conditions
Melt Flow Rate (at 230°C, 2.16 kgf) ¹¹	6	g/10 min	ASTM D1238
Density ¹¹	1.13	g/cm³	ASTM D792
Density ¹¹	1.12	g/cm³	ISO 1183
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.5 - 1.7	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.51 - 1.67	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.5 - 1.7	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.51 - 1.67	%	ISO 294

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield) ¹¹	28	MPa	ISO 527
Tensile Stress (Break) ¹¹	26	MPa	ISO 527
Tensile Strain (Yield) ¹¹	7	%	ISO 527
Tensile Strain (Break) ¹¹	40	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2160	MPa	ISO 527
Flexural Stress ¹¹	3.00E+01	MPa	ISO 178
Flexural Modulus ¹¹	1600	MPa	ISO 178

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	130	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	94	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	3	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	215 - 220	°C	—
Front - Zone 3 Temperature ⁷	205 - 215	°C	—
Middle - Zone 2 Temperature ⁷	200 - 210	°C	—
Rear - Zone 1 Temperature ⁷	195 - 205	°C	—
Mold Temperature ⁷	30 - 50	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 