Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Ball Indentation Hardness (H358/30) ¹¹ | 96 | MPa | ISO 2039-1 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2300 | MPa | ASTM D790 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2300 | MPa | ISO 178 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 88 | MPa | ASTM D790 |
Flexural Stress (Yield, at 2 mm/min) ¹¹ | 80 | MPa | ISO 178 |
Hardness (Rockwell R) ¹¹ | 115 | — | ISO 2039-2 |
Taber Abrasion (CS-17, 1 kg) ¹¹ | 63 | mg/1000cy | ASTM D1044 |
Tensile Modulus (at 1 mm/min) ¹¹ | 2400 | MPa | ISO 527 |
Tensile Modulus (at 5 mm/min) ¹¹ | 2270 | MPa | ASTM D638 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 100 | % | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | min. 50 | % | ISO 527 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 100 | % | ASTM D638 |
Tensile Strain (Yield, 5 mm/min) ¹¹ | 5 | % | ISO 527 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 4 | % | ISO 527 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 45 | MPa | ISO 527 |
Tensile Stress (Break, 50 mm/min) ¹¹ | 45 | MPa | ISO 527 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 47 | MPa | ASTM D638 |
Tensile Stress (Yield, 5 mm/min) ¹¹ | 55 | MPa | ISO 527 |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 55 | MPa | ISO 527 |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.15 | g/cm³ | ISO 1183 |
Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ | 24 | g/10 min | ASTM D1238 |
Melt Volume Rate (at 260°C, 2.16 kg) ¹¹ | 8 | cm³/10 min | ISO 1133 |
Melt Volume Rate (at 260°C, 5.0 kg) ¹¹ | 22 | cm³/10 min | ISO 1133 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.2 | % | ISO 62 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Specific Gravity ¹¹ | 1.15 | — | ASTM D792 |
Water Absorption (at 23°C, saturated) ¹¹ | 0.6 | % | ISO 62-1 |
Value | Units | Test Method / Conditions | |
Ball Pressure Test (at 123°C to 127°C, by VDE) ¹¹ | Pass | — | IEC 60695-10-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000072 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000072 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 112 | °C | ASTM D648 |
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 102 | °C | ISO 75/Ae |
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 122 | °C | ISO 75/Be |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 105 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ISO 8302 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 128 | °C | ISO 306 |
Vicat Softening Temperature (Rate B/50) ¹¹ | 130 | °C | ASTM D1525 |
Vicat Softening Temperature (Rate B/50) ¹¹ | 126 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
Comparative Tracking Index ʳ ¹¹ | 250 | V | IEC 60112 |
Dielectric Strength (in oil, at 0.8mm) ¹¹ | 35 | kV/mm | IEC 60243-1 |
Dielectric Strength (in oil, at 1.6mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17 | kV/mm | IEC 60243-1 |
Dissipation Factor (at 50/60 Hz) ¹¹ | 0.002 | — | IEC 60250 |
Dissipation Factor (at at 1 MHz) ¹¹ | 0.007 | — | IEC 60250 |
High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1.2 | mm | UL 746A |
Hot Wire Ignition (PLC 3) ¹¹ | min. 1.2 | mm | UL 746A |
Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
Relative Permittivity (50/60 Hz) ¹¹ | 2.8 | — | IEC 60250 |
Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
Volume Resistivity ¹¹ | min. 1.E+15 | Ω.cm | IEC 60093 |
Value | Units | Test Method / Conditions | |
Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eA |
Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 50 | kJ/m² | ISO 179/1eA |
Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 54 | J | ASTM D3763 |
Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 30 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, at -30°C) ¹¹ | 480 | J/m | ASTM D256 |
Izod Impact (Notched, at 23°C) ¹¹ | 580 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 100-110 | °C | — |
Drying Time ⁷ | 2 - 4 | Hrs | — |
Front - Zone 3 Temperature ⁷ | 250 - 290 | °C | — |
Hopper Temperature ⁷ | 60 - 80 | °C | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 260 - 290 | °C | — |
Middle - Zone 2 Temperature ⁷ | 250 - 290 | °C | — |
Mold Temperature ⁷ | 60 - 90 | °C | — |
Nozzle Temperature ⁷ | 240 - 280 | °C | — |
Rear - Zone 1 Temperature ⁷ | 230 - 260 | °C | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
Glow Wire Flammability Index (at 3.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
Glow Wire Ignitability Temperature (at 3.5 mm) ᵖ | 725 | °C | IEC 60695-2-13 |
Oxygen Index (LOI) ᵖ | 23 | % | ISO 4589 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability