LNP™ ELCRES™ FXE9111T

Identification & Functionality

Additives Included

Flame Retardant,

Mold Release Agent,

UV Stabilizer

Polymer Name

Polycarbonate-Siloxane Copolymer

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free

Materials Features

Excellent Aesthetics,

Flame Retardant,

Good Aesthetics,

Good Colorability,

Good Mold Release,

Good Processability,

Good Surface Appearance,

High Ductility,

High Durability,

High Impact Resistance,

Low Temperature Impact Resistance,

Non-brominated,

Non-chlorinated,

Pigmentable,

UV Stabilized,

Unreinforced

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Lighting

Consumer Goods — Housewares

Printing & Packaging — Packaging

Industrial & Transport Packaging,

Non-Food Consumer Packaging

Electrical & Electronics — Parts & Components

Housings & Enclosures

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Interior Parts,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Covers,

Displays,

Electrical/Electronic Applications,

Enclosure,

Home Appliances,

Home Decoration,

Home Decors,

Household Goods,

Housings,

Lighting Applications,

Rigid Packaging,

Tablets,

Toys,

White Goods & Small Appliances

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Custom,

Transparent

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	57	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	54	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	92	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2190	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	90	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	89	MPa	ASTM D790
Flexural Stress (at 5% strain, 1.3 mm/min, 50 mm span) ¹¹	85	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2180	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹	58	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	5	%	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	52	MPa	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	95	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2230	MPa	ISO 527
Flexural Stress (at 3.5% strain, 2 mm/min) ¹¹	67.4	MPa	ISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹	7.5	%	ISO 178
Flexural Strength (at 2 mm/min) ¹¹	86.6	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2190	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.2	—	ASTM D792
Density ¹¹	1.201	g/cm³	ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹	0.11	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.04	%	ISO 62-4
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	19.5	g/10 min	ASTM D1238
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	18.3	cm³/10 min	ASTM D1238
Mold Shrinkage (flow) ᵍ ¹¹	0.66	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.73	%	SABIC method

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	119	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	107	°C	ASTM D648
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	119	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	107	°C	ISO 75/Af
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.000075	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 95°C, xflow) ¹¹	0.000083	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.000081	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.000086	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate A/50) ¹¹	132	°C	ASTM D1525
Vicat Softening Temperature (Rate B/120) ¹¹	126	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	126	°C	ASTM D1525
Vicat Softening Temperature (Rate B/50) ¹¹	125	°C	ISO 306
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	2150	J/m	ASTM D4812
Izod Impact (Notched, at 0°C) ¹¹	500	J/m	ASTM D256
Izod Impact (Notched, at 23°C) ¹¹	777	J/m	ASTM D256
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	57	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	180	kJ/m²	ISO 180/1U
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	130	kJ/m²	ISO 179/1eU
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	59	kJ/m²	ISO 179/1eA

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	90	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	250 - 285	°C	—
Nozzle Temperature ⁷	250 - 285	°C	—
Front - Zone 3 Temperature ⁷	250 - 285	°C	—
Middle - Zone 2 Temperature ⁷	250 - 285	°C	—
Rear - Zone 1 Temperature ⁷	250 - 285	°C	—
Mold Temperature ⁷	50 - 90	°C	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 2.0	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America