LNP™ LUBRICOMP™ Compound CZL36

Identification & Functionality

Additives Included

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Styrenics

Fillers Included

Glass Fiber,

Milled Glass Fiber,

PTFE

Polymer Name

Polystyrene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Materials Features

Dimensional Stability,

Friction Resistant,

Good Mold Release,

High Impact Performance,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures,

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Interior Parts,

Building Materials,

Cell Phones,

Computer Components,

Construction Applications,

Consumer Applications,

Displays,

Electrical/Electronic Applications,

Faucet System Components,

Fittings,

Gears,

Industrial Applications,

Pump Parts,

Sporting Goods,

Tablets,

Water Management

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield) ¹¹	24	MPa	ASTM D638
Tensile Stress (Yield) ¹¹	22	MPa	ISO 527
Tensile Stress (Break) ¹¹	24	MPa	ASTM D638
Tensile Stress (Break) ¹¹	21	MPa	ISO 527
Tensile Strain (Yield) ¹¹	1.7	%	ASTM D638
Tensile Strain (Yield) ¹¹	1.6	%	ISO 527
Tensile Strain (Break) ¹¹	2.3	%	ASTM D638
Tensile Strain (Break) ¹¹	3.5	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	2550	MPa	ASTM D638
Flexural Stress ¹¹	52	MPa	ASTM D790
Flexural Stress ¹¹	49	MPa	ISO 178
Flexural Modulus ¹¹	4890	MPa	ASTM D790
Flexural Modulus ¹¹	5110	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	3880	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.52	g/cm³	ISO 1183
Density ¹¹	1.52	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.03	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2 - 0.3	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.24 - 0.26	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.3 - 0.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.31 - 0.37	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.09	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	83	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000649	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000065	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000674	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000675	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	83	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	117	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	26	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	2	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	7	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	2	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	250	°C	—
Front - Zone 3 Temperature ⁷	265 - 275	°C	—
Middle - Zone 2 Temperature ⁷	245 - 255	°C	—
Rear - Zone 1 Temperature ⁷	220 - 230	°C	—
Mold Temperature ⁷	40 - 65	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 