LNP LUBRICOMP™ Compound - RFL36L - SABIC's Specialty

Identification & Functionality

Features & Benefits

Labeling Claims: Food Contact Acceptable
Materials Features: Food Contact Acceptable,
Friction Resistant,
High Stiffness,
Low Extractables,
Low Leachable,
Wear Resistant

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Consumer Goods,
Electrical & Electronics,
Healthcare & Pharma,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Powertrain & UTH
Building & Construction — Building Materials
Pipes & Plumbing
Electrical & Electronics — Devices & Assemblies
Consumer Electronics
Healthcare & Pharma — Medical
Medical Devices & Assemblies
Printing & Packaging — Packaging
Food & Beverage Packaging,
Industrial & Transport Packaging,
Non-Food Consumer Packaging
Plastics & Elastomers End Uses: Appliances,
Automotive Gears,
Building Materials,
Consumer Applications,
Food Packaging,
Home Appliances,
Hoses,
Medical Devices,
Pipes,
Water Management
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Density ¹¹	1.52	g/cm³	ISO 1183
Density ¹¹	1.52	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.4 - 0.6	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.53	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.3 - 1.5	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.4	%	ISO 294
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.4	%	ASTM D570
Wear Factor Washer ¹¹	4	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.66	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.65	—	ASTM D3702 Modified: Manual

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	260	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	247	°C	ISO 75/Af
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000288	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000029	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000738	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000074	1/°C	ISO 11359-2
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	261	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	252	°C	ASTM D648

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80104, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	61	kJ/m²	ISO 180/1U
Multi-Axial Impact ¹¹	2	J	ISO 6603
Izod Impact (Notched, at 23°C) ¹¹	96	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	1009	J/m	ASTM D4812
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	12	J	ASTM D3763

Packaging & Availability

LNP™ LUBRICOMP™ Compound RFL36L