LNP LUBRICOMP™ Compound - RFN16 - SABIC's Specialty

Identification & Functionality

Additives Included: Lubricant (Molybdenum Disulfide),
Lubricant (Unspecified),
Mold Release Agent
Chemical Family: Polyamides
Fillers Included: Glass Fiber,
Molybdenum Disulfide
Polymer Name: Polyamide 66 (PA 66)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polyamides

Features & Benefits

Labeling Claims: No Added PFAS
Materials Features: Friction Resistant,
Good Mold Release,
High Stiffness,
Lubricated,
No Added PFAS,
Wear Resistant

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Home Appliances,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications,
Windows
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 HB
Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	155	MPa	ASTM D638
Tensile Stress (Yield, 5 mm/min) ¹¹	168	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.1	%	ISO 527
Tensile Strain (Break) ¹¹	2.9	%	ASTM D638
Tensile Modulus (at 1 mm/min) ¹¹	9100	MPa	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	9560	MPa	ASTM D638
Flexural Stress (Yield, at 2 mm/min) ¹¹	237	MPa	ISO 178
Flexural Stress ¹¹	206	MPa	ASTM D790
Flexural Modulus (at 2 mm/min) ¹¹	8900	MPa	ISO 178
Flexural Modulus ¹¹	7130	MPa	ASTM D790

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000025	1/°C	ISO 11359-2
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	205	°C	ASTM D648
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.00012	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	260	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	249	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ LUBRICOMP™ Compound RFN16