LNP LUBRICOMP™ Compound - RI001 - SABIC's Specialty

Identification & Functionality

Features & Benefits

Materials Features: Friction Resistant,
Lubricated,
Non-Halogenated,
UL Listed,
Unreinforced,
Wear Resistant

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Home Appliances,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications,
Windows
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 HB
Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	61	MPa	ASTM D638
Tensile Stress (Yield, 5 mm/min) ¹¹	6.90E+01	MPa	ISO 527
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.6	%	ASTM D638
Tensile Stress (Break, 5 mm/min) ¹¹	57	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	68	MPa	ISO 527
Tensile Modulus (at 5 mm/min) ¹¹	3200	MPa	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2910	MPa	ASTM D790
Tensile Strain (Break, 5 mm/min) ¹¹	4.4	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	58	%	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	85	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2300	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2690	MPa	ISO 178
Tensile Strain (Yield, 5 mm/min) ¹¹	3.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2930	MPa	ISO 527
Flexural Stress ¹¹	96	MPa	ISO 178

	Value	Units	Test Method / Conditions
Density ¹¹	1.14	g/cm³	ASTM D792
Density ¹¹	1.14	g/cm³	ISO 1183
Specific Gravity ¹¹	1.15	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	1.2	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	2 - 4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2 - 4	%	ASTM D955
Wear Factor Washer ¹¹	104	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Wear Factor Ring ¹¹	-1	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.43	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.26	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	1.5	%	ISO 62

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000097	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000133	1/°C	ISO 11359-2
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	241	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	66	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000083	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.00008	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	164	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	59	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	214	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, at 23°C) ¹¹	1630	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	45	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	6	J	ASTM D3763

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ LUBRICOMP™ Compound RI001