LNP™ LUBRICOMP™ Compound SFP36

Identification & Functionality

Additives Included

Heat Stabilizer,

Lubricant (Unspecified),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

PTFE,

PTFE/Silicone,

Silicone

Polymer Name

Polyamide 12 (PA 12)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Friction Resistant,

Good Mold Release,

Heat Stabilized,

High Stiffness,

Low Moisture Absorption,

Lubricated,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Automotive & Transportation — Transportation

Off Road & Recreational Vehicle (RV)

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Under The Hood,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Displays,

Electrical/Electronic Applications,

Home Appliances,

Industrial Applications,

Recreational Vehicle Components,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	125	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	117	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	3.2	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3.2	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	9060	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	178	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	176	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	7510	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	129	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	129	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2.9	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	9070	MPa	ISO 527
Flexural Stress ¹¹	191	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7920	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.39	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.15	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.1 - 0.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Wear Factor Washer ¹¹	14	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Wear Factor Ring ¹¹	0	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.67	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.52	—	ASTM D3702 Modified: Manual
Density ¹¹	1.38	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.22	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	177	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	172	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000028	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.00008	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	177	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	169	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	1000	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	146	J/m	ASTM D256
Multi-Axial Impact ¹¹	3	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	9	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	58	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	14	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.12 - 0.2	%	—
Melt Temperature ⁷	225 - 240	°C	—
Front - Zone 3 Temperature ⁷	225 - 240	°C	—
Middle - Zone 2 Temperature ⁷	220 - 230	°C	—
Rear - Zone 1 Temperature ⁷	215 - 225	°C	—
Mold Temperature ⁷	70 - 80	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 