LNP™ LUBRICOMP™ Compound UCL16AS

Identification & Functionality

Additives Included

Heat Stabilizer,

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Carbon Fiber,

PTFE

Polymer Name

Polyphthalamide (PPA)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Electrically Conductive,

Friction Resistant,

Good Mold Release,

Heat Stabilized,

High Stiffness,

High Strength,

High Temperature Resistance,

Light Weight,

Very Good Heat Resistance,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Under The Hood,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Displays,

Electrical/Electronic Applications,

Heavy Vehicles,

Home Appliances,

Industrial Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	272	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.4	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	21800	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	373	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	19000	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.36	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000007	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000046	1/°C	ISO 11359-2

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	40	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	7	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15	%	—
Melt Temperature ⁷	315 - 330	°C	—
Front - Zone 3 Temperature ⁷	325 - 340	°C	—
Middle - Zone 2 Temperature ⁷	315 - 325	°C	—
Rear - Zone 1 Temperature ⁷	310 - 320	°C	—
Mold Temperature ⁷	150 - 170	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 