LNP™ STAT-KON™ Compound CD000I

Identification & Functionality

Additives Included

Heat Stabilizer,

Impact Modifier

Chemical Family

Styrenics

Fillers Included

Carbon Black,

Carbon Powder

Polymer Name

Polystyrene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Materials Features

Electrically Conductive,

Heat Stabilized,

High Impact Performance,

High Impact Resistance,

Impact Modified

Applications & Uses

Markets

Electrical & Electronics,

Industrial

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Electrical/Electronic Applications,

Electronic Components,

Industrial Applications,

Semiconductor Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	20	MPa	ASTM D638
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	23	MPa	ASTM D638
Tensile Strain (Break) ¹¹	6.6	%	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	16	MPa	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2170	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	1.2	%	ASTM D638
Flexural Stress ¹¹	40	MPa	ISO 178
Flexural Stress ¹¹	41	MPa	ASTM D790
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	9.7	%	ASTM D638
Flexural Modulus ¹¹	2690	MPa	ASTM D790
Tensile Modulus (at 5 mm/min) ¹¹	2280	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	42	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2280	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	23	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	17	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	1.2	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	7.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2120	MPa	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	2100	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.08	g/cm³	ASTM D792
Specific Gravity ¹¹	1.08	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.1	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.3 - 0.7	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.4 - 0.7	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.13	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	75	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	87	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000098	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000107	1/°C	ASTM E831
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	87	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	78	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ᵈ ¹¹	100 - 1000000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	384	J/m	ASTM D4812
Izod Impact (Unnotched, at 23°C) ¹¹	744	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	48	J/m	ASTM D256
Izod Impact (Notched, at 23°C) ¹¹	82	J/m	ASTM D256
Multi-Axial Impact ¹¹	15	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	18	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	31	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	250	°C	—
Front - Zone 3 Temperature ⁷	265 - 275	°C	—
Middle - Zone 2 Temperature ⁷	245 - 255	°C	—
Rear - Zone 1 Temperature ⁷	220 - 230	°C	—
Mold Temperature ⁷	40 - 65	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94

Note

• ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• North America