LNP™ STAT-KON™ Compound DEF13

Identification & Functionality

Chemical Family

Polycarbonate (PC)

Fillers Included

Carbon Fiber,

Glass Fiber

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Materials Features

ESD Protection,

Electrically Conductive,

High Stiffness,

High Strength,

Light Weight,

UL Listed

Applications & Uses

Markets

Electrical & Electronics,

Industrial

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Electrical/Electronic Applications,

Industrial Applications,

Semiconductor Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0,

UL 94 V1

Mechanical Properties

	Value	Units	Test Method / Conditions
Flexural Strength (at 2 mm/min) ¹¹	211	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	18500	MPa	ISO 178
Tensile Stress (Yield, 5 mm/min) ¹¹	44	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	12	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.9	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	12410	MPa	ISO 527
Tensile Stress (Break) ¹¹	118	MPa	ASTM D638
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	61	MPa	ASTM D638
Tensile Strain (Break) ¹¹	4	%	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	159	MPa	ASTM D790
Tensile Modulus (at 50 mm/min) ¹¹	17870	MPa	ASTM D638
Flexural Modulus ¹¹	9440	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.29	g/cm³	ISO 1183
Density ¹¹	1.29	g/cm³	ASTM D792
Specific Gravity ¹¹	1.29	—	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.07	%	ASTM D570

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	148	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	144	°C	ISO 75/Ae
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	147	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	144	°C	ASTM D648
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ᵈ ¹¹	100 - 1000000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	13	kJ/m²	ISO 180/1A
Izod Impact (Notched, at 23°C) ¹¹	101	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C, 6.4mm) ¹¹	513	J/m	ASTM D4812

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	305 - 325	°C	—
Front - Zone 3 Temperature ⁷	320 - 330	°C	—
Middle - Zone 2 Temperature ⁷	310 - 320	°C	—
Rear - Zone 1 Temperature ⁷	295 - 305	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Maximum Moisture Content ⁷	0.02	%	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 3	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ᵖ	min. 1.5	mm	UL 94

Note

• ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance