LNP STAT-KON™ Compound - DEL22P - SABIC's Specialty - PC

Identification & Functionality

Additives Included: Lubricant (PTFE),
Mold Release Agent
Chemical Family: Polycarbonate (PC)
Fillers Included: Carbon Fiber,
PTFE
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Materials Features: ESD Protection,
Electrically Conductive,
Friction Resistant,
Good Mold Release,
Good Processability,
High Flowability,
High Stiffness,
High Strength,
Light Weight,
Wear Resistant

Applications & Uses

Markets: Electrical & Electronics,
Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Industrial Automation
Electrical & Electronics — Parts & Components
Semiconductor Manufacturing
Plastics & Elastomers End Uses: Electrical/Electronic Applications,
Industrial Applications,
Semiconductor Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Density ¹¹	1.3	g/cm³	ISO 1183
Density ¹¹	1.3	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.1	%	ASTM D570
Mold Shrinkage (flow, 0.75-2.3 mm) ᵍ ¹¹	0.1 - 0.3	%	SABIC method
Mold Shrinkage (flow) ᵍ ¹¹	0.1 - 0.3	%	SABIC method
Mold Shrinkage (xflow, 0.75-2.3 mm) ᵍ ¹¹	0.4 - 0.6	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.4 - 0.6	%	SABIC method
Wear Factor Washer ¹¹	15	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.55	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.52	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.18	%	ISO 62

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	134	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000014	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000015	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000076	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000076	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	143	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	100	Ω.cm	IEC 60093
Surface Resistivity (ROA) ¹¹	100 - 1000000	Ω	IEC 60093

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	283	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	74	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	1.30E+01	J	ASTM D3763
Multi-Axial Impact ¹¹	102	J	ISO 6603
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	34	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	6	kJ/m²	ISO 180/1A

Packaging & Availability

LNP™ STAT-KON™ Compound DEL22P