LNP STAT-KON™ Compound - DX09315C - SABIC's Specialty

Identification & Functionality

Additives Included: Mold Release Agent
Chemical Family: Polycarbonate (PC)
Fillers Included: Carbon Fiber
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Materials Features: Electrically Conductive,
Good Flow,
Good Mold Release,
Good Processability,
High Stiffness,
High Strength,
Light Weight,
Low Liquid Particle Count,
Low Outgassing

Applications & Uses

Markets: Electrical & Electronics,
Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Industrial Automation
Electrical & Electronics — Parts & Components
Semiconductor Manufacturing
Plastics & Elastomers End Uses: Electrical/Electronic Applications,
Flat Panel Display (FPD),
Industrial Applications,
Semiconductor Applications,
Wireless Communication
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 HB
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	123	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	9810	MPa	ASTM D638
Flexural Stress ¹¹	201	MPa	ASTM D790
Flexural Modulus ¹¹	8130	MPa	ASTM D790

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	125	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000013	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.00007	1/°C	ASTM E831
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	10000 - 500000	Ω	ASTM D257

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	732	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	94	J/m	ASTM D256

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 1	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ STAT-KON™ Compound DX09315C