LNP™ STAT-KON™ Compound EX02598C

Identification & Functionality

Additives Included

Heat Stabilizer

Chemical Family

Polyetherimide (PEI),

Polyimides (PI)

Fillers Included

Carbon Nanotube

Polymer Name

Polyether Imide (PEI)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Dimensional Stability,

ESD Protection,

Electrically Conductive,

Heat Stabilized,

High Temperature Resistance,

Low Liquid Particle Count,

Low Outgassing,

Very Good Heat Resistance

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Cell Phones,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Industrial Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	52	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.7	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	3410	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	98	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	3310	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	60	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	3240	MPa	ISO 527
Flexural Stress ¹¹	72	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	3110	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.27	—	ASTM D792
Density ¹¹	1.26	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.6 - 0.8	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	172	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	163	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.00005	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000054	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	171	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	160	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	1000 - 1000000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	266	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	19	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	2	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	18	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	2	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Extended Drying Temperature ⁷	150	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	360 - 400	°C	—
Rear - Zone 1 Temperature ⁷	360 - 380	°C	—
Middle - Zone 2 Temperature ⁷	370 - 390	°C	—
Front - Zone 3 Temperature ⁷	380 - 400	°C	—
Nozzle Temperature ⁷	390 - 400	°C	—
Mold Temperature ⁷	140 - 180	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed (Circumferential speed) ⁷	0.2 - 0.3	m/s	—
Vent Depth ⁷	0.025 - 0.076	mm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 