LNP™ STAT-KON™ Compound EX03319C

Identification & Functionality

Additives Included

Mold Release Agent

Chemical Family

Polyetherimide (PEI),

Polyimides (PI)

Fillers Included

Carbon Fiber

Polymer Name

Polyether Imide (PEI)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Electrically Conductive,

Good Mold Release,

High Stiffness,

High Strength,

High Temperature Resistance,

Light Weight,

Low Liquid Particle Count,

Low Outgassing,

No Added PFAS,

Very Good Heat Resistance

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Cell Phones,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	224	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.3	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	16960	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	233	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	11600	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.351	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.2	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.05 - 0.15	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.3 - 0.45	%	ASTM D955

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	205	°C	ASTM D648

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ᵈ ¹¹	5000 - 5000000	Ω.cm	ASTM D257
Surface Resistivity ᵈ ¹¹	5000 - 500000	Ω	ASTM D257
Static Decay (at 5000V to max. 50V) ¹¹	max. 0.1	Seconds	FTMS101B

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	354	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	48	J/m	ASTM D256
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	4	kJ/m²	ISO 179/1eA
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	22	kJ/m²	ISO 179/1eU

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	150	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	360 - 400	°C	—
Rear - Zone 1 Temperature ⁷	360 - 380	°C	—
Middle - Zone 2 Temperature ⁷	370 - 390	°C	—
Front - Zone 3 Temperature ⁷	380 - 400	°C	—
Nozzle Temperature ⁷	390 - 400	°C	—
Mold Temperature ⁷	140 - 180	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed (Circumferential speed) ⁷	0.2 - 0.3	m/s	—
Vent Depth ⁷	0.025 - 0.076	mm	—

Note

• ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 