LNP™ STAT-KON™ Compound MX18001J

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Carbon Powder

Polymer Name

Polypropylene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

Food Contact Acceptable,

No Added PFAS

Materials Features

Electrically Conductive,

Food Contact Acceptable,

Low Extractables

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Healthcare & Pharma,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Materials

Pipes & Plumbing

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Food & Beverage Packaging,

Healthcare Packaging,

Non-Food Consumer Packaging

Plastics & Elastomers End Uses

Appliances,

Consumer Applications,

Food Packaging,

Hoses,

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging,

Pipes

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Flexural Modulus (1.3 mm/min, 50 mm span)⁴⁹	2750	MPa	ASTM D790
Flexural Modulus (2 mm/min)⁴⁹	2600	MPa	ISO 178
Flexural Strength (1.3 mm/min, 50 mm span)⁴⁹	54	MPa	ASTM D790
Flexural Strength (2 mm/min)⁴⁹	55	MPa	ISO 178
Tensile Modulus (1 mm/min)⁴⁹	2700	MPa	ISO 527
Tensile Modulus (5 mm/min)⁴⁹	2950	MPa	ASTM D638
Tensile Strain at Break (5 mm/min)⁴⁹	1.7	%	ISO 527
Tensile Strain at Break (Type I, 5 mm/min)⁴⁹	2.1	%	ASTM D638
Tensile Stress at Break (5 mm/min)⁴⁹	30	MPa	ISO 527
Tensile Stress at Break (Type I, 5 mm/min)⁴⁹	30	MPa	ASTM D638

Physical Properties

	Value	Units	Test Method / Conditions
Density⁴⁹	1.08	g/cm³	ISO 1183
Moisture Absorption (at 23°C/50% RH/24hrs)⁴⁹	max. 0.1	%	ISO 62-4
Moisture Absorption (at 23°C/50% RH/Equilibrium)⁴⁹	max. 0.1	%	ISO 62-4
Mold Shrinkage - flow¹²,⁴⁹	1.3 - 1.7	%	SABIC method
Mold Shrinkage - xflow¹²,⁴⁹	1.1 - 1.5	%	SABIC method
Water Absorption (at 23°C/24hrs)⁴⁹	max. 0.1	%	ISO 62-1
Water Absorption (at 23°C/Saturated)⁴⁹	max. 0.1	%	ISO 62-1

Thermal Properties

	Value	Units	Test Method / Conditions
CTE - flow (at 23°C to 60°C)⁴⁹	0.0001	1/°C	ISO 11359-2
CTE - flow (at -40°C to 60°C)⁴⁹	7.9e-05	1/°C	ASTM E831
CTE - xflow (at 23°C to 60°C)⁴⁹	0.00011	1/°C	ISO 11359-2
CTE - xflow (at -40°C to 60°C)⁴⁹	8.6e-05	1/°C	ASTM E831
HDT - Unannealed (0.45 MPa, 3.2 mm)⁴⁹	122	°C	ASTM D648
HDT - Unannealed (1.82 MPa, 3.2mm)⁴⁹	70	°C	ASTM D648
HDT/Af (1.8 MPa Flatw 80*10*4 sp=64mm)⁴⁹	74	°C	ISO 75/Af
HDT/Bf (0.45 MPa Flatw 80*10*4 sp=64mm)⁴⁹	121	°C	ISO 75/Bf

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity⁸,⁴⁹	100.0 - 10000.0	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact Notched (80*10*4 +23°C)⁴⁹	1	kJ/m²	ISO 180/1A
Izod Impact Notched (at 23°C)⁴⁹	10	J/m	ASTM D256
Izod Impact Unnotched (80*10*4 +23°C)⁴⁹	20	kJ/m²	ISO 180/1U
Izod Impact Unnotched (at 23°C)⁴⁹	250	J/m	ASTM D4812

Injection Molding

	Value	Units	Test Method / Conditions
Back Pressure⁴²	0.2 - 0.3	MPa	—
Drying Temperature⁴²	80	°C	—
Drying Time⁴²	4	Hrs	—
Front - Zone 3 Temperature⁴²	240 - 250	°C	—
Melt Temperature⁴²	225 - 250	°C	—
Middle - Zone 2 Temperature⁴²	215 - 225	°C	—
Mold Temperature⁴²	30 - 50	°C	—
Rear - Zone 1 Temperature⁴²	195 - 205	°C	—
Screw Speed⁴²	30 - 60	rpm	—

Note

• ⁴² Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ⁴⁹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ⁸ Measurement meets requirements as specified in ASTM D4496.
• ¹² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.