LNP™ THERMOCOMP™ Compound 2X95787

Identification & Functionality

Chemical Family

Fluoropolymers,

Polyolefins

Fillers Included

Glass Fiber

Polymer Name

Ethylene Tetrafluoroethylene Copolymer (ETFE)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Cost Effective,

High Modulus,

High Stiffness

Applications & Uses

Markets

Electrical & Electronics,

Healthcare & Pharma,

Industrial

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Healthcare & Pharma — Medical

Tubing & Fluids Handling

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Industrial — Power, Water & Utilities

Renewable Energy

Plastics & Elastomers End Uses

Electrical/Electronic Applications,

Energy Management,

Industrial Applications,

Semiconductor Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield) ¹¹	48	MPa	ASTM D638
Tensile Stress (Yield) ¹¹	47	MPa	ISO 527
Tensile Stress (Break) ¹¹	45	MPa	ISO 527
Tensile Stress (Break) ¹¹	45	MPa	ASTM D638
Tensile Strain (Yield) ¹¹	9.3	%	ASTM D638
Tensile Strain (Yield) ¹¹	8.6	%	ISO 527
Tensile Strain (Break) ¹¹	13.7	%	ASTM D638
Tensile Strain (Break) ¹¹	12.8	%	ISO 527
Tensile Modulus (at 5 mm/min) ¹¹	4270	MPa	ASTM D638
Flexural Modulus ¹¹	4000	MPa	ISO 178
Flexural Modulus ¹¹	3400	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	4050	MPa	ISO 527
Flexural Stress ¹¹	66	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.84	g/cm³	ASTM D792
Density ¹¹	1.83	g/cm³	ISO 1183
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.8	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.8	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2.4	%	ISO 294

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	222	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	107	°C	ASTM D648
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	203	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	91	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	1335	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	480	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	19	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	83	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	2.40E+01	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 150	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	315	°C	—
Melt Temperature ⁷	370 - 390	°C	—
Front - Zone 3 Temperature ⁷	330 - 345	°C	—
Front - Zone 3 Temperature ⁷	390 - 400	°C	—
Middle - Zone 2 Temperature ⁷	310 - 320	°C	—
Middle - Zone 2 Temperature ⁷	355 - 365	°C	—
Rear - Zone 1 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	315 - 325	°C	—
Mold Temperature ⁷	95 - 120	°C	—
Mold Temperature ⁷	140 - 165	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 