LNP THERMOCOMP™ Compound - EX11414 - SABIC's Specialty

Identification & Functionality

Additives Included: Flame Retardant,
Mold Release Agent
Chemical Family: Polyetherimide (PEI),
Polyimides (PI)
Fillers Included: Carbon Fiber
Polymer Name: Polyether Imide (PEI)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Cost Effective,
Electrically Conductive,
Flame Retardant,
Good Mold Release,
High Stiffness,
High Strength,
High Temperature Resistance,
Light Weight,
Very Good Heat Resistance

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Consumer Goods,
Electrical & Electronics
Applications: Automotive & Transportation — Automotive
Powertrain & UTH
Building & Construction — Building Envelope & Roofing
Glazing & Window Elements
Building & Construction — Building Materials
Interior Fixtures
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Automotive & Transportation — Transportation
Aerospace & Aviation
Plastics & Elastomers End Uses: Aerospace Applications,
Automotive Applications,
Automotive Under The Hood,
Building Materials,
Construction Applications,
Consumer Applications,
Electrical Components,
Electrical/Electronic Applications,
Sporting Goods
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	230	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	17380	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	308	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	14600	MPa	ASTM D790

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.33	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.23	%	ASTM D570
Poisson's Ratio ¹¹	0.44	—	ASTM E132

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	213	°C	ASTM D648

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	10000 - 100000	Ω	ASTM D257

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	598	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	78	J/m	ASTM D256

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	150	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	360 - 400	°C	—
Rear - Zone 1 Temperature ⁷	360 - 380	°C	—
Middle - Zone 2 Temperature ⁷	370 - 390	°C	—
Front - Zone 3 Temperature ⁷	380 - 400	°C	—
Nozzle Temperature ⁷	390 - 400	°C	—
Mold Temperature ⁷	140 - 180	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed (Circumferential speed) ⁷	0.2 - 0.3	m/s	—
Vent Depth ⁷	0.025 - 0.076	mm	—

Regulatory & Compliance

Packaging & Availability

LNP™ THERMOCOMP™ Compound EX11414