LNP THERMOCOMP™ Compound - LC003E - SABIC's Specialty

Identification & Functionality

Chemical Family: Polyether Ether Ketone (PEEK)
Fillers Included: Carbon Fiber
Polymer Name: Polyetheretherketone (PEEK)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Cost Effective,
ESD Protection,
Easy To Mold,
Electrically Conductive,
Good Moldability,
Good Processability,
High Stiffness,
High Strength,
High Temperature Resistance,
Light Weight,
UL Listed,
Very Good Heat Resistance

Applications & Uses

Markets: Consumer Goods,
Electrical & Electronics,
Industrial
Applications: Consumer Goods — Appliances & Electronics
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays,
Industrial Automation,
Lighting
Electrical & Electronics — Parts & Components
Connectors,
Semiconductor Manufacturing,
Switches & Relays
Plastics & Elastomers End Uses: Cell Phones,
Computer Components,
Displays,
Electrical Components,
Electrical/Electronic Applications,
Industrial Applications,
Non-LED Lighting,
Semiconductor Applications,
Tablets
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Density ¹¹	1.33	g/cm³	ISO 1183
Density ¹¹	1.33	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.07	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2 - 0.3	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.28 - 0.31	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.5 - 0.6	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.51 - 0.58	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.13	%	ISO 62

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	270	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000052	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000519	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000536	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000536	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	298	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	1000 - 10000000	Ω	ASTM D257

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	400	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	37	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	4	J	ASTM D3763
Multi-Axial Impact ¹¹	1	J	ISO 6603
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	29	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

Packaging & Availability

LNP™ THERMOCOMP™ Compound LC003E