LNP™ THERMOCOMP™ Compound LC004XXP

Identification & Functionality

Chemical Family

Polyether Ether Ketone (PEEK)

Fillers Included

Carbon Fiber

Polymer Name

Polyetheretherketone (PEEK)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

ESD Protection,

Electrically Conductive,

High Stiffness,

High Strength,

Light Weight,

No Added PFAS,

Very Good Heat Resistance

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Cell Phones,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	199	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.9	%	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	280	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	13900	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	0.1 - 0.3	%	SABIC method
Density ¹¹	1.36	g/cm³	ISO 1183

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	100 - 10000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	45	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 150	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.1	%	—
Melt Temperature ⁷	380 - 390	°C	—
Front - Zone 3 Temperature ⁷	380 - 395	°C	—
Middle - Zone 2 Temperature ⁷	365 - 375	°C	—
Rear - Zone 1 Temperature ⁷	350 - 360	°C	—
Mold Temperature ⁷	140 - 165	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	60 - 100	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

ATEX Directives

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America