LNP™ THERMOCOMP™ Compound LF002XXP-WT02005

Identification & Functionality

Chemical Family

Polyether Ether Ketone (PEEK)

Fillers Included

Glass Fiber

Polymer Name

Polyetheretherketone (PEEK)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Cost Effective,

High Stiffness,

High Temperature Resistance,

Very Good Heat Resistance

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Appliances,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Industrial Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Custom

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	110	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2.6	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	8550	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	170	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7500	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	0.4 - 0.6	%	SABIC method
Density ¹¹	1.88	g/cm³	ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹	0.04	%	ISO 62-1

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000028	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000042	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	179	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	30	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 150	°C	-
Drying Time ⁷	4	Hrs	-
Maximum Moisture Content ⁷	0.1	%	-
Melt Temperature ⁷	380 - 390	°C	-
Front - Zone 3 Temperature ⁷	380 - 395	°C	-
Middle - Zone 2 Temperature ⁷	365 - 375	°C	-
Rear - Zone 1 Temperature ⁷	350 - 360	°C	-
Mold Temperature ⁷	140 - 165	°C	-
Back Pressure ⁷	0.3 - 0.7	MPa	-
Screw Speed ⁷	60 - 100	rpm	-

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 