LNP™ THERMOCOMP™ Compound SC004

Identification & Functionality

Chemical Family

Polyamides

Fillers Included

Carbon Fiber

Polymer Name

Polyamide 12 (PA 12)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

ESD Protection,

Electrically Conductive,

High Stiffness,

High Strength,

Light Weight,

Low Moisture Absorption,

No Added PFAS

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Appliances,

Automotive Under The Hood,

Cell Phones,

Commercial Appliance,

Computer Components,

Displays,

Electrical/Electronic Applications,

Home Appliances,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	130	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2 - 4	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	10300	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	171	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7900	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.11	g/cm³	ISO 1183

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	100 - 10000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	50	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	14	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	100 - 105	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	260 - 280	°C	—
Nozzle Temperature ⁷	250 - 270	°C	—
Front - Zone 3 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	250 - 270	°C	—
Rear - Zone 1 Temperature ⁷	240 - 260	°C	—
Hopper Temperature ⁷	40 - 60	°C	—
Mold Temperature ⁷	60 - 85	°C	—

Note

• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

ATEX Directives