LNP THERMOCOMP™ Compound - SF00A - SABIC's Specialty

Identification & Functionality

Features & Benefits

Labeling Claims: No Added PFAS
Materials Features: Cost Effective,
Good Mold Release,
High Modulus,
High Stiffness,
No Added PFAS

Applications & Uses

Markets: Automotive & Transportation,
Consumer Goods,
Electrical & Electronics,
Industrial
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Electrical & Electronics — Parts & Components
Semiconductor Manufacturing
Plastics & Elastomers End Uses: Appliances,
Automotive Applications,
Automotive Under The Hood,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Displays,
Electrical Components,
Electrical/Electronic Applications,
Home Appliances,
Industrial Applications,
Semiconductor Applications,
Tablets
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	121	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	121	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	1.7	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.7	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	12800	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	217	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	217	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	10984	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	113	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	113	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	1.5	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.5	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	12280	MPa	ISO 527

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	176	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	166	°C	ASTM D648

Packaging & Availability

LNP™ THERMOCOMP™ Compound SF00A