LNP™ THERMOTUF™ Compound V1000UXC

Identification & Functionality

Additives Included

Heat Stabilizer,

Impact Modifier,

Mold Release Agent,

UV Stabilizer

Chemical Family

Polyamides

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Good Mold Release,

Good Surface Appearance,

Good UV Stability,

Good Weather Stability,

Heat Stabilized,

High Durability,

High Impact Resistance,

Impact Modified,

No Added PFAS,

UV Resistant,

UV Stabilized,

Unreinforced

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Construction Applications,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Front Spoiler,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Side Spoiler,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	39	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	39	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	57.2	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	84.5	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	1710	MPa	ASTM D638
Flexural Stress ¹¹	55	MPa	ASTM D790
Flexural Stress ¹¹	53	MPa	ISO 178
Flexural Modulus ¹¹	2060	MPa	ASTM D790
Flexural Modulus ¹¹	1700	MPa	ISO 178
Tensile Stress (Yield, 5 mm/min) ¹¹	41	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	41	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	146.7	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	165	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	1650	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.07	—	ASTM D792
Density ¹¹	1.08	g/cm³	ISO 1183
Density ¹¹	1.065	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.6	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	2.2	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	2.1 - 2.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2.5 - 2.7	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2.6	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	1	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	192	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	193	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000135	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000134	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000133	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000134	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	150	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	147	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Multi-Axial Impact ¹¹	49	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	49	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	270 - 295	°C	—
Front - Zone 3 Temperature ⁷	290 - 300	°C	—
Middle - Zone 2 Temperature ⁷	270 - 280	°C	—
Rear - Zone 1 Temperature ⁷	260 - 270	°C	—
Mold Temperature ⁷	50 - 95	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	10 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 