Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Processing Information (Extrusion Blow Molding)
- Impact Properties
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 48 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 72 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2410 | MPa | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.7 | % | SABIC method |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 82 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 95 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 95 | °C | UL 746B |
| Value | Units | Test Method / Conditions | |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
| Value | Units | Test Method / Conditions | |
| Adapter - Zone 5 Temperature | 210 - 215 | °C | — |
| Barrel - Zone 1 Temperature | 205 - 215 | °C | — |
| Barrel - Zone 2 Temperature | 205 - 215 | °C | — |
| Barrel - Zone 3 Temperature | 205 - 215 | °C | — |
| Barrel - Zone 4 Temperature | 210 - 215 | °C | — |
| Die Temperature | 215 - 220 | °C | — |
| Drying Temperature | 95 | °C | — |
| Drying Time | 2 - 4 | Hrs | — |
| Head - Zone 6 - Top Temperature | 210 - 215 | °C | — |
| Head - Zone 7 - Bottom Temperature | 215 - 220 | °C | — |
| Melt Temperature (Parison) | 210 - 215 | °C | — |
| Mold Temperature | 50 - 70 | °C | — |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 267 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 106 | J/m | ASTM D256 |
| Color (at 23°C) ¹¹ | 13 | J | ASTM D3029 |
| Color (at -40°C) ¹¹ | 33 | J | ASTM D3029 |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 3 | mm | UL 94 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability