NORYL™ Resin PKN4752

Identification & Functionality

Polymer Name

PPE/GPPS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Food Contact Acceptable

Materials Features

Amorphous,

Dimensional Stability,

Food Contact Acceptable,

High Hydrolytic Stability,

High Temperature Resistance,

Low Moisture Absorption,

Low Shrinkage,

Low Specific Gravity,

Low Warpage,

Translucent,

Unreinforced,

Very Good Heat Resistance

Applications & Uses

Markets

Electrical & Electronics,

Industrial,

Printing & Packaging

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Printing & Packaging — Packaging

Food & Beverage Packaging,

Industrial & Transport Packaging,

Non-Food Consumer Packaging

Plastics & Elastomers End Uses

Audio Equipment,

Bottles,

Consumer Applications,

Electrical/Electronic Applications,

Electronic Components,

Flexible Packaging,

Food Containers,

Food Packaging,

Industrial Applications,

Masterbatch Base Resin,

Masterbatches,

Thin Walled Packaging

Plastics & Elastomers Processing Methods

Extrusion,

Profile Extrusion,

Sheet Extrusion

Properties

Color

Translucent,

Transparent

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 50 mm/min) ¹¹	86	MPa	ISO 527
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	86	MPa	ASTM D638
Tensile Strain (Break, 50 mm/min) ¹¹	6	%	ISO 527
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	73	MPa	ASTM D638
Tensile Modulus (at 1 mm/min) ¹¹	3100	MPa	ISO 527
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	6.00E+00	%	ASTM D638
Flexural Stress (Yield, at 2 mm/min) ¹¹	130	MPa	ISO 178
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	15	%	ASTM D638
Flexural Modulus (at 2 mm/min) ¹¹	2950	MPa	ISO 178
Tensile Modulus (at 50 mm/min) ¹¹	3000	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	144	MPa	ASTM D790
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹	136	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	3150	MPa	ASTM D790
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹	2940	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.08	g/cm³	ISO 1183
Specific Gravity ¹¹	1.08	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.6 - 0.9	%	SABIC method

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (Rate A/50) ¹¹	174	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	163	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	147	°C	ISO 75/Ae
Vicat Softening Temperature (Rate B/50) ¹¹	173	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	160	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	151	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	151	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000063	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000558	1/°C	ASTM E831

Processing Information (Sheet Extrusion)

	Value	Units	Test Method / Conditions
Adapter Temperature	240 - 265	°C	—
Barrel - Zone 1 Temperature	205 - 225	°C	—
Barrel - Zone 2 Temperature	215 - 240	°C	—
Barrel - Zone 3 Temperature	240 - 265	°C	—
Barrel - Zone 4 Temperature	240 - 265	°C	—
Die Temperature	240 - 265	°C	—
Drying Temperature	70 - 80	°C	—
Drying Time	2 - 4	Hrs	—
Drying Time (Cumulative)	8	Hrs	—
Maximum Moisture Content	0	%	—
Melt Temperature	265 - 275	°C	—
Roll Stack Temperature - Bottom	105 - 120	°C	—
Roll Stack Temperature - Middle	105 - 120	°C	—
Roll Stack Temperature - Top	105 - 120	°C	—

Processing Information (Profile Extrusion)

	Value	Units	Test Method / Conditions
Drying Temperature	80 - 95	°C	—
Drying Time	2 - 4	Hrs	—
Melt Temperature	280 - 300	°C	—
Barrel - Zone 1 Temperature	215 - 240	°C	—
Barrel - Zone 2 Temperature	225 - 250	°C	—
Barrel - Zone 3 Temperature	250 - 275	°C	—
Barrel - Zone 4 Temperature	250 - 275	°C	—
Hopper Temperature	50 - 70	°C	—
Adapter Temperature	250 - 275	°C	—
Die Temperature	250 - 275	°C	—
Calibrator Temperature	60 - 80	°C	—

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	3	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹	3	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	2	kJ/m²	ISO 179/1eA
Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	2	kJ/m²	ISO 179/1eA
Izod Impact (Notched, at 23°C) ¹¹	32	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	6	J	ASTM D3763

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

FDA Compliant

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America