NORYL™ Resin N300X

Identification & Functionality

Additives Included

Flame Retardant,

Impact Modifier

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free,

No Added PFAS

Materials Features

Amorphous,

Dimensional Stability,

Flame Retardant,

High Hydrolytic Stability,

Impact Modified,

Low Moisture Absorption,

Low Shrinkage,

Low Specific Gravity,

Low Warpage,

No Added PFAS,

Non-Halogenated,

Non-brominated,

Non-chlorinated,

Unreinforced

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Consumer Goods — Lawn & Garden

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Industrial — Power, Water & Utilities

Renewable Energy

Plastics & Elastomers End Uses

Building Materials,

Connectors,

Electrical Components,

Electrical/Electronic Applications,

Enclosure,

Energy Management,

Front Spoiler,

Garden Equipment,

Lawn Equipment,

Pool Covers,

Side Spoiler,

Solar Panels,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 5VA,

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	74	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	73	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	5.3	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	7.6	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2380	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	110	MPa	ASTM D790
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹	110	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2650	MPa	ASTM D790
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹	2500	MPa	ASTM D790
Hardness (Rockwell R) ¹¹	119	—	ASTM D785
Tensile Stress (Yield) ¹¹	75	MPa	ISO 527
Tensile Stress (Break) ¹¹	66	MPa	ISO 527
Tensile Strain (Yield) ¹¹	5.2	%	ISO 527
Tensile Strain (Break) ¹¹	13	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2220	MPa	ISO 527
Flexural Stress ¹¹	112	MPa	ISO 178
Flexural Modulus ¹¹	2520	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.1	—	ASTM D792
Water Absorption (at 23°C, saturated) ¹¹	0.06	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Mold Shrinkage (on Tensile Bar, xflow) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹	7.4	g/10 min	ASTM D1238
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹	7	cm³/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	155	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	140	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	145	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.00008	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.00008	1/°C	ASTM E831
Vicat Softening Temperature (Rate B/50) ¹¹	162	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	164	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	156	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	140	°C	ISO 75/Ae
Relative Temperature Index (Electrical) ᵖ ¹¹	105	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	105	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	105	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	1.00E+17	Ω.cm	ASTM D257
Surface Resistivity ¹¹	1.00E+17	Ω	ASTM D257
Dielectric Strength (in oil, at 3.2mm) ¹¹	19.4	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	2.68	—	ASTM D150
Relative Permittivity (1 MHz) ¹¹	2.63	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.0031	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.009	—	ASTM D150
High Voltage Arc Track Rate (PLC) ᵖ ¹¹	4	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ᵖ ¹¹	3	PLC Code	UL 746A
High Ampere Arc Ignition (PLC 0) ᵖ ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 4) ᵖ ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 0) ᵖ ¹¹	min. 3	mm	UL 746A
Hot Wire Ignition (PLC 2) ᵖ ¹¹	min. 1.5	mm	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	6	PLC Code	ASTM D495

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	190	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	55	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	54	J	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	15	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	110 - 120	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	300 - 325	°C	—
Nozzle Temperature ⁷	300 - 325	°C	—
Front - Zone 3 Temperature ⁷	290 - 325	°C	—
Middle - Zone 2 Temperature ⁷	275 - 320	°C	—
Rear - Zone 1 Temperature ⁷	265 - 315	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	20 - 100	rpm	—
Shot to Cylinder Size ⁷	30 - 70	%	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94-5VA Flame Class Rating) ᵖ ¹¹	min. 2	mm	UL 94
UL Recognized (94V-0 Flame Class Rating) ᵖ ¹¹	min. 1.5	mm	UL 94
Glow Wire Flammability Index (at 1.5 mm) ¹¹	960	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 2 mm) ¹¹	960	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 3 mm) ¹¹	960	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature (at 1.0 mm) ¹¹	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 1.5 mm) ¹¹	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 2.0 mm) ¹¹	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 3.0 mm) ¹¹	800	°C	IEC 60695-2-13

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• North America