Features & Benefits
- Materials Features
- Features and Benefits
Crestamould® VE 690PA has excellent blister resistance and significantly reduces the occurrence of print through, to produce durable mouldings with an enhanced surface finish.
Applications & Uses
- Applications
- Applications
Crestamould® VE 690PA was developed for use as a skin coat in tooling and marine applications where surface finish is critical.
- Formulation
Crestamould® VE 690PA must be thoroughly stirred and allowed to attain workshop temperature (18°C - 20°C) before use. It needs only the addition of a catalyst to start the curing reaction. Butanox M50, Butanox LA-IN and Trigonox 249VR catalyst can be used, which should be added into the resin.
Properties
- Color
- Typical Liquid Resin Properties
- Resin Properties - Unfilled Casting (Cured)
- Notes
* Curing Schedule - 24hrs at 20°C, 16hrs at 40°C.
** Curing Schedule - 24hrs at 20°C, 3hrs at 80°C .
† Curing Schedule - 24hrs at 20°C, 5 hrs at 80°C, 3 hrs at 120°C.
Value | Units | Test Method / Conditions | |
Viscosity (at 25°C, 37.35 s⁻¹) | 5 | Poise | — |
Viscosity (at 25°C, 4500 s⁻¹) | 2.3 | Poise | — |
Stability (in dark at 25°C) | 6 | Months | — |
Gel Time (at 20°C, using 2% Butanox M50) | 15 | Minutes | — |
Specific Gravity (at 25°C) | 1.065 | g/cm³ | — |
Gel Time (at 20°C, using 2% LA-IN) | 24 | Minutes | — |
Gel Time (at 20°C, using 2% Triganox 249VR) | 21 | Minutes | — |
Value | Units | Test Method / Conditions | |
Barcol Hardness (GYZJ 934 - 1)* | 23 | — | — |
Deflection Temperature (under load 1.80 MPa)* | 60 | ºC | — |
Water Absorption (24h, at 23°C)* | 10 | mg | — |
Tensile Strength* | 60 | MPa | — |
Tensile Modulus* | 2.7 | GPa | — |
Elongation (at break)* | 4.3 | % | — |
Specific Gravity (at 25°C)* | 1.161 | g/cm³ | — |
Barcol Hardness (GYZJ 934 - 1)** | 35 | — | — |
Deflection Temperature under load (1.80 MPa)† | 94 | ºC | — |
Water Absorption (24h, at 23°C)** | 15 | mg | — |
Tensile Strength** | 52 | MPa | — |
Tensile Modulus** | 3 | GPa | — |
Elongation (at break)** | 2.1 | % | — |
Specific Gravity (at 25°C)** | 1.158 | g/cm³ | — |
Regulatory & Compliance
- Approvals
Crestamould® VE 690PA is approved by Lloyd’s Register of Shipping for use in the construction of craft under their survey.
Technical Details & Test Data
- Crestamould® Matched Tooling Systems
Crestamold® VE 690PA has excellent blister resistance and significantly reduces the occurrence of print through, to produce durable moldings with an enhanced surface finish.
- Additives
The addition of pigment, fillers or other additives may adversely affect the resin properties. Users should consult Scott Bader’s Technical Service Department before making any such additions.
Packaging & Availability
- Regional Availability
- Packaging
Crestamould® VE 690PA is supplied in 25kg and 200kg steel containers.
Storage & Handling
- Storage
Crestamould® VE 690PA should be stored in the dark in suitable closed containers. It is recommended that the storage temperature should be less than 20°C where practical, but should not exceed 30°C. Ideally, containers should be opened only immediately prior to use.