Crystic Pipe Relining Resin PD10098T - 6122

Identification & Functionality

Chemical Family: Orthophthalics,
Unsaturated Polyester (UPE)
Polymer Name: Thermoset Polyester
Composite Materials Functions: Resins, Binders & Matrix Materials,
Surface Finish
Technologies: Composite Materials
Product Families: Composite Materials — Polymers & Resins
Thermoset Resins
Composite Materials — Surface Finishes
Gelcoats & Topcoats

Features & Benefits

Materials Features: Chemical Resistant,
Good Mechanical Properties,
Good Reactivity,
High Elongation,
High Heat Deflection Temperature,
High Impact Resistance,
High Molecular Weight,
Thixotropic,
Water Resistant
Features and Benefits: High HDT

High molecular weight

High elongation

Excellent mechanical properties

Excellent resistance to water ingress

Excellent impact resistance

Applications & Uses

Markets: Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Composites End Use: Liners,
Pipes,
Tanks
Recommended Applications: CRYSTIC PD10098T has been specially developed for the production of liners to be used in the pipe relining industry. Fully cured laminates offer high chemical resistance and mechanical properties, together with excellent long term property retention.
Formulation Guidelines: The following formulations are recommended for hot curing (80 – 85°C)

CRYSTIC PD10098T :100 parts 100parts

Perkadox 16 : 0.5 - 1 % 0,5 – 1%

Trigonox C : 1 – 1.5 %

Trigononox 42S : - 1 – 1,5%

Accelerator NL49P : 0,3 – 0,5% 0,3 – 0,5%

Perkadox 16, Trigonox C and Trigonox 42S are products from AKZO. Accelerator NL49P is a Cobalt accelerator (1% active Cobalt) from AKZO

Properties

Typical Liquid Resin Properties
Cured Properties
Note: Test according to Iso 75A, ISO EN 178 & EN 527
1MPa = 1MN/m² = 1N/mm² = 10,2 kgf/cm²
(*): cured 24 h at 20°C then 3 h à 80°C except for the HDT where the schedule was 24 h at 20°C then 5 h at 80°C then 3h at 100°C.

	Value	Units	Test Method / Conditions
Viscosity (at 25°C, Brookfield RVT, Sp4, 5 rpm)	40 - 50	dPa.s	—
Thixotropic Index (5/50 rpm)	3.0 - 4.0	—	—
Specific Gravity (at 25°C)	1.1	—	—
Acid Index	12 - 16	mg KOH/g	—
Volatile Content	40 - 44	%	—
Stability (with storage recommendations)	9	Months	—
Gel Time (at 82°C, 1.0 % perkadox 16)	3 - 5	Minutes	—
Peak Temperature	200 - 250	°C	—
Stability (at 20°C, 1% Perkadox 16)	min. 20	Hours	—

	Value	Units	Test Method / Conditions
Barcol Hardness (GYZJ 934 – 1)*	45	—	—
Heat Deflection Temperature (1.8 MPa)*	98	°C	—
Specific Gravity (at 20°C)*	1.16	—	—
Elongation (at break)*	2.6	%	—
Tensile Strength*	69	MPa	—
Tensile Modulus*	3550	MPa	—
Flexural Strength*	130	MPa	—
Flexural Modulus*	3600	MPa	—

Regulatory & Compliance

Quality Standards: DIN 16946-2,
DIN 18820
Approvals: CRYSTIC PD10098T is type 1140 according to the German standard DIN 16946 Teil 2 and group 3 according to DIN 18820 Teil 1.

Technical Details & Test Data

Reactivity: The ambient temperature, the quantity and the type of catalyst will control the reactivity of the resin. The time to peak of CRYSTIC PD10098T with 0.8% Perkadox 16 and 1% Trigonox C at 80°C is 7 to 8 minutes.
Additives: Since certain pigments, fillers or extra styrene may the affect properties of CRYSTIC PD10098T their effect should be evaluated before addition to the formulation.

Packaging & Availability

Packaging Type: Totes (IBC)
Packaging: Crystic® PD10098T is supplied in 225 kg or 1100 kg containers. Bulk supplies can be delivered by road tanker.

Storage & Handling

Storage: CRYSTIC PD10098T should be stored between 5°C and 25°C in the original, unopened container in a dry, well ventilated place. Protect from freezing and direct sunlight. Avoid contact with oxidizing agents. If stored outside of these recommendations, shelf life will be significantly reduced. CRYSTIC PD10098T should be periodically stirred to avoid sedimentation during the storage period.

Crystic® Pipe Relining Resin PD10098T