Identification & Functionality
- Chemical Family
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Features and Benefits
- Isophthalic neopentyl base resin
- High elongation
- Special monomers
- Easy to apply
- Low styrene content
- Excellent water / blistering resistance
- Good impact resistance
- Only 24 % styrene, 28 % VOC
- Excellent surface finish
- Less exposure to the environment and workers
Applications & Uses
- Markets
- Application Method
- Composites Processing Methods
- Spray Application
Do Don’t Ensure the gelcoat has attained workshop temperature of 15°C - 25°C before use. Stir the gelcoat with high shear mixers as this will temporarily break down the thixotropy leading to drainage. Add 2% Butanox® M-50 or equivalent catalyst. Exceed a wet film thickness of 800 microns as thick films encourage air retention. Gently stir the gelcoat by hand or low shear stirrer. Apply excessive thickness in corner areas as this can cause pre-release Spray at the minimum practical pressure whilst maintaining an acceptable spray pattern and full fan width. Apply backing laminate before the gelcoat has reached an appropriate degree of cure. Apply a mist coat and then build up thickness in long, even passes of 100 - 150 microns until the recommended wet film thickness of 600 – 800 microns is reached. Catalyze more gelcoat than can be applied before it starts to gel. Apply the first layer of laminate within 24 hours of the gelcoat. Allow vapor to be retained in deep mold sections as this can cause slow curing. - Spray Set Up
Application temperature 15 - 25°C Catalyst 2% Butanox® M-50 or equivalent catalyst.
Nozzle airless gun 423 - 535 Pressure 3 to 4.5 bars Distance to mold 50 cm minimum Wet Film Thickness 600 - 800 microns
Properties
- Cured Properties
- Uncured Properties
- Note
* Curing Schedule - 24hrs at 20°C, 3hrs at 80°C.
† Curing Schedule - 24hrs at 20°C, 5hrs at 80°C, 3hrs at 120°C.- Gel time & Backup time
Catalyst level and temperature will influence the gel time. The product only requires the addition of catalyst to start curing. We recommend the use of a 50% MEKP (type Butanox® M-50) which should be added at 2% in the gelcoat.
Temperature Gel time (2% MEKP 50%)** Backup time (2% MEKP 50%)** 20°C 13 minutes 60 minutes 23°C 10 minutes 50 minutes 30°C 8 minutes 40 minutes **Measured under laboratory conditions. Information should be used as a guide only.
Crystic Ecogel uses innovative monomers. When the back up time is reached, the glass reinforcement can be laid down even if the gelcoat seems still tacky. This tackiness is part of the chemical formulation of the gelcoat.
| Value | Units | Test Method / Conditions | |
| Barcol Hardness (Model GYZJ 934-1)* | 40 | — | EN59 |
| Water Absorption (24h, at 23°C)* | 18 | mg | BS EN ISO 62 part 6.2 |
| Heat Deflection Temperature (1.8 MPa)† | 56 | °C | BS EN ISO 75-2 (1996) |
| Elongation (at break)* | 4 | % | BS EN ISO 527-2 |
| Tensile Strength* | 68 | MPa | BS EN ISO 527-2 |
| Tensile Modulus* | 3100 | MPa | BS EN ISO 527-2 |
| Flexural Strength* | 120 | MPa | BS EN ISO 178 |
| Flexural Modulus* | 3400 | MPa | BS EN ISO 178 |
| Value | Units | Test Method / Conditions | |
| Viscosity (at 23°C, Brookfield Sp5, 2.5 rpm) | 350 - 450 | dPa.s | — |
| Styrene Content | 24 | % | — |
| Thixotropic Index (2.5/20 rpm) | 5.80 - 6.50 | — | — |
| Specific Gravity (at 25°C) | 1.3 | — | — |
Technical Details & Test Data
- Recommended Testing
- It is recommended that customers test all gelcoats before use under their own conditions of application to ensure that the product meets requirements.
- Post Curing
- Satisfactory laminates for many applications can be made with Crystic Ecogel® S3PA by curing at workshop temperature (15°C - 25°C). However, for optimum properties, laminates must be post-cured before being put into service. The molding should be allowed to cure for 24 hours at workshop temperature and then oven-cured for 16 hours at 40°C
- Additives and Variants
The information contained in this technical data sheet applies to all pigmented versions. Incorporation of additional material may affect the working, weathering or cured properties of the gelcoat. Please check with Scott Bader’s Technical Service department before using the gelcoat outside of specified parameters.
Packaging & Availability
- Packaging Type
- Packaging Information
Crystic Ecogel® S3PA is available in 25kg and 225kg containers.
Storage & Handling
- Shelf Life
- 5 Months
- Storage Conditions
Crystic Ecogel S3PA should be stored in its original container, under cover, and out of direct sunlight. These must be kept closed and airtight. It is recommended that the storage temperature should be less than 25ºC and the product should not be frozen. Storing the product outside of these conditions may affect the properties of the product and reduce its shelf life. Ideally, containers should be opened only immediately prior to use. Material should be used within 5 months from the date of production.