Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- FEATURES
- FDA compliant for incidental and direct food contact.
- 100% solids, no solvents, and no VOCs.
- Fast-set; handle in two minutes or less.
- Extended tack time to allow deep surface penetration.
- High dry temperature stability to 250°F (121°C) with
- intermittent temperatures up to 300°F (148°C).
Applications & Uses
- Applications
- Application Area
- Application Method
- RECOMMENDED USES
- Direct and incidental food contact.
- Coating for steel or other substrate exposed to food.
- Liner for concrete tanks, ponds, lagoons, reservoirs, dikes, tunnels, barges, etc.
- Replace or repair failed existing sheet membrane liners.
- Steel tanks, silos, and pipes.
- Encapsulation for EPS or other types of flotation materials.
- Encapsulation for asbestos, lead paint, or other dry hazardous materials (Consult SPI).
- Earthen containment used with or without geotextile.
- Concrete parking decks.
- GENERAL APPLICATION INSTRUCTIONS
Apply POLYSHIELD HT™ SLOW FC to only clean, dry, sound surfaces free of loose particles or other foreign matter. A primer may be required; subject to type and condition ofthe substrate. POLYSHIELD HT™ SLOW FC can be sprayedover a broad range of ambient temperatures. It is recommended that POLYSHIELD HT™ SLOW FC be sprayed in multi-directional (north-south/east-west) passes to ensure uniform thickness. The polyol “B” component must be thoroughly power mixed each day, prior to use.
- MIXING & THINNING
- The polyol “B” component must be thoroughly power mixed each day, prior to use. Thinning is not required.
- Using any thinner may adversely affect product performance.
Properties
- Wet Properties
Value | Units | Test Method / Conditions | |
Solids by Volume | 100 | % | — |
Solids by Weight | 100 | % | — |
Volatile Organic Compounds (0 g/l) | 0 | lbs./gal. | — |
Theoretical Coverage DFT (16 mils/gal) | 100 | sq. ft. | — |
Weight per gallon (approx.) | 8.9 (4.0) | lbs. (kg) | — |
Number of Coats | 1 - 2 | — | — |
Mix Ratio | 1 “A” : 1 “B” | — | — |
Viscosity | A: 350 ± 50 (B: 475 ± 50) | cPs | — |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- PROCESSING EQUIPMENT & SETTINGS
- Standard 1:1 ratio, heated, plural-component equipment developing a minimum of 2000 psi (10.4 MPa) dynamic pressure at the gun with heating capabilities to 170°F(77°C) will adequately spray HARD CAP™ 100.
- Machines capable of producing a higher dynamic psimay be required depending on the service environment the HARD CAP™ 100 will be exposed to.
- Proportioning machine primary heater temperature 160-170°F (71-77°C).
- Hose temperature 160-170°F (71-76°C). A hose thermometer inserted under the insulation near the gun should read a minimum of 145-155°F (63-68°C).
- Physical properties will be enhanced when sprayed at higher pressure (3000 psi or more); and utilizing an impingement mix gun such as MP Fusion or GX7-DI gun.
- Do not use mixing chambers with output greater than 1.5 gallons per minute.
- LIMITATIONS
- POLYSHIELD HT™ SLOW FC is for professional use only.
- User must be proficient in the application of POLYSHIELD HT™ SLOW FC and the use of the high pressure heated plural component equipment used to apply it.
- POLYSHIELD HT™ SLOW FC must be stored at temperatures between 60—90°F (15—32°C).
- Liquid temperature in containers/drums during application 70—100°F (21—38°C).
- Apply POLYSHIELD HT™ SLOW FC when surface and air temperatures are above 40°F (5°C) and the surface temperature is at least 5°F (3°C) above dew point and rising.
- Avoid moisture contamination in containers. Containers should not be resealed if contamination is suspected.CO2 created pressure can develop. Do not attempt to use contaminated material.
- Undried air exposed to liquid components will reduce physical properties of the cured coating.
Note: The material supplied is a two component system(component “A”/component “B”, which is used to formulatethis product. The quality and characteristics of the finished polymer is determined by the mixture and application of thetwo components by the person applying the polymers.
- DRY PROPERTIES*
@ 34 mils (0.8 mm) Tensile Strength ASTM D638 ± 3,966 psi (28 mpa) Elongation ASTM D638 ± 526% Hardness (Shore A) ASTM D2240-81 42 ± 5 100 % Modulus ASTM D412 1,127 psi (8 mpa) ± 100 300 % Modulus ASTM D412 2,000 psi (14 mpa) ± 100 Tear Resistance ASTM D624 457 PLI (80 KN/m) ± 50 Service Temperature -60°F - +250° (-50°C - +121°C) *All cured film properties are approximate since processing parameter, ad-mixture types, and quantities change physical properties of the cured elastomer. All samples for above tests were force cured 48 hours or aged for more than three weeks. It is recommended that the user perform their own independent testing.
- CURING SCHEDULE
Gel ± 30 sec Tack Free ± 1 min. 30 sec. Post Cure** 24 hours
Recoat 0 - 12 hours
** Complete polymerization to achieve final strength can take up to several days or weeks, depending on a variety of conditions or product type. All samples for above tests were force cured 48 hours or aged for more than three weeks. It is recommended that the user perform their own independent testing.
The samples for tests were sprayed with Graco HXP3 @ 2500 psi dynamic (17 mpa). Primaries/Hose Heat 170°F (77°C,) MP Fusion gun with 29/29 mixing chamber with .040 ceramtip. Test results from SPI.- TEST INFORMATION
ABRASION RESISTANCE ASTM D4060 1000 g - 1000 cycles H-18 wheel 36 mg. loss CS-17 wheel 5.3 mg. loss FDA Extraction Test 21 CFR 175.300(e)(4)(i) 2 hours at 250°F 0.27 mg/in2
Packaging & Availability
- Packaging Type
- COLORS
POLYSHIELD HT™ SLOW FC is available in SPI standard colors (Sand, Medium Gray, and Black).
Note: POLYSHIELD HT™ SLOWFC is an aromatic polyurea; therefore, as with all aromaticscolor change and superficial oxidation will occur. Aliphaticurethane and other suitable topcoats can be used wherelong-term color stability and increased longevity in full sunexposure are of critical importance.
- PACKAGING
This product sold in standard 110 gallon drum and 550gallon tote sets. Available in other container sizes, Non-standardcontainers may require a longer lead time.
Storage & Handling
- Shelf Life
- 6 Months