Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Typical Applications
- Gas distribution pipes.
Properties
- Color
- Mechanical Properties
- Physical Properties
- Note
- The above properties values are not to be construed as specifications.
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (at -30°C) | 15 | kJ/m2 | ISO 179 |
Charpy Notched Impact Strength (at 23°C) | 29 | kJ/m2 | ISO 179 |
Flexural Creep Modulus(4 Point loading method, 1 min-value) | 1100 | MPa | DIN 19537-2 |
Flexural Creep Modulus(4 Point loading method, 2000 h-value) | 330 | MPa | DIN 19537-2 |
Flexural Creep Modulus(4 Point loading method, 24 h-value) | 560 | MPa | DIN 19537-2 |
Flexural Stress (at 3,5% deflection) | 20 | MPa | ISO 178 |
FNCT (4.0 MPa, 2% Arkopal N 100, 80°C) | min.1000 | h | ISO 16770 |
Injection Molding Melt Temperature | 200 - 280 | °C | — |
Maximum Elongation TD | min.350 | % | EN 638 |
Melt Temperature | 190 - 220 | °C | — |
MRS Classification | 10 | MPa | ISO/TR 9080 |
Oxidation Induction Time (OIT, 210°C) | min. 30 | minute | EN 728 |
Shore Hardness (Shore D, 3 sec) | 62 | — | ISO 868 |
Tensile Creep Modulus 1000h | 350 [2.0] | MPa | ISO 899-1 |
Tensile Creep Modulus 1h | 800 [2.0] | MPa | ISO 899-1 |
Tensile Modulus (at 23°C, v = 1mm/min, Secant) | 850 | MPa | ISO 527-1,-2 |
Tensile Strain at Yield (at 23°C, v = 50 mm/min) | 9 | % | ISO 527-1,-2 |
Tensile Stress at Yield (at 23°C, v = 50 mm/min) | 23 | MPa | ISO 527-1,-2 |
Value | Units | Test Method / Conditions | |
Density | 0.951 | g/cm3 | ISO 1183 |
Melt Flow Rate (190°C / 21.6 kg) | 6.4 | g/10 min | ISO 1133 |
Melt Flow Rate (190°C / 5kg) | 0.23 | g / 10 min | ISO 1133 |
Staudinger Index Jg | 380 | ml/g | ISO 1628 |
Vicat Softening Temperature (VST/B/50 K/h (50N)) | 74 | °C | ISO 306 |
Safety & Health
- Safety
- Workers should be protected from the possibility of skin or eye contact with molten polymer. As minimum precaution, safety glasses and heat resistance gloves are suggested to prevent mechanical or thermal injury to eyes and hands. Molten polymer exceeding processing condition requirements may degrade and release, fumes, vapors and unpleasant odor. In higher concentrations they may cause irritation of the mucus membranes. Fabrication areas should be ventilated to carry away fumes and vapors. Legislation on the control of emissions and pollution prevention must be observed. If the principles of sound manufacturing practice are adhered to and the place of work is well ventilated, no health hazards are involved in processing the material. The material may burn when supplied with excess heat and oxygen. It should be handled and stored away from contact with direct flames and/or ignition sources. In burning the material generates considerable heat and may release a dense black smoke. Fires should be extinguished by heavy foams or dry powder. For further information about safety in handling and processing please refer to the Material Safety Data Sheet (MSDS).
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage
- The material is packed in 25 kg bags or in bulk containers protecting it from contamination. Storage time of material longer than 6 months may have a negative influence on the quality of the final product. It is generally recommended to convert all materials latest within 6 months from delivery date. The material is subjected to degradation by ultra-violet radiation or by high storage temperatures. Therefore the material must be protected from direct sunlight, temperatures above 40°C and high atmospheric humidity during storage. Further unfavorable storage conditions are large fluctuations in ambient temperature and high atmospheric humidity. These conditions may lead to moisture condensing inside the packaging. Under these circumstances, it is recommended to dry the material before use. After a storage period of more than 3 months, drying of such material is recommended as standard practice. TASNEE will not give any warranty to unfavorable storage conditions which may lead to quality deterioration such as color change, bad smell and inferior product performance.