Products

VINNOL® E 15/48 A is a hydroxyl-containing copolymer composed of approximately 84 wt.% vinyl chloride (VC) and 16 wt.% acrylic acid esters. It serves as a binder in surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNOL® E 22/48 A is a copolymer composed of approximately 75 wt.% vinyl chloride (VC) and 25 wt.% carbon acid esters with hydroxyl functionality. It serves as a binder for surface coating compounds and printing inks. As a thermoplastic and physically drying binder, VINNOL® E 22/48 A undergoes film formation as the solvent within the formulation evaporates.

VINNOL® E 15/40 A is a hydroxyl-containing copolymer comprising approximately 84 wt.% vinyl chloride (VC) and 16 wt.% acrylic acid esters. Its primary application lies in serving as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNOL® E 18/38 is a copolymer consisting of approximately 82 wt.% vinyl chloride (VC) and 18 wt.% vinyl acetate (VAc). It is primarily utilized as a binder in printing inks and surface coating compounds. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNAPAS® SAF 72 is a fine-particle-sized dispersion of a styrene/acrylic acid ester copolymer in water with a solids content of 50%. It is manufactured without using coalescent, organic solvents, plasticizers, or alkyl phenol ethoxylate (APEO)-containing compounds. It exhibits excellent penetration into porous substrates and offers great flexibility.

VINNOL® E 15/45 is a copolymer composed of approximately 85 wt.% vinyl chloride (VC) and 15 wt.% vinyl acetate (VAc). It serves as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNAPAS® SAF 34 is a fine-particle dispersion of a special styrene/acrylate copolymer. It is produced without the use of alkyl phenol ethoxylate (APEO)-containing compounds. VINNAPAS® SAF 34 exhibits excellent pigment binding properties, great adhesion to inorganic substrates, very good water resistance, excellent alkali resistance, very low dirt pick-up, and great versatility.

VINNOL® E 15/45 M is a carboxylate-containing terpolymer consisting of approximately 84 wt.% vinyl chloride (VC), 15 wt.% vinyl acetate (VAc), and 1 wt.% dicarboxylic acid. It functions primarily as a binder in surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNAPAS® SAF 608 is a water-based dispersion containing a fine-particle-sized copolymer of styrene and acrylic acid ester. It has a solid content of 50%. This product is manufactured without the inclusion of coalescents, organic solvents, plasticizers, or compounds containing alkyl phenol ethoxylate (APEO). It exhibits excellent penetration into porous substrates and offers great flexibility.

VINNOL® H 11/59 is a copolymer composed of approximately 89 wt.% vinyl chloride (VC) and 11 wt.% vinyl acetate (VAc). Its primary application lies in serving as a binder for surface coating compounds and printing inks. As a thermoplastic and physically drying binder, VINNOL® H 11/59 undergoes a film-forming process when the solvent within the formulation evaporates.