Products

LINCORE® FF P1 400 is a 100% flax fabric made of untwisted rovings. The molding can be realized by Infusion, Resin Transfer Molding, Resin Film Infusion Lay up. These fabrics are also availble as resin-impregnated reinforcements for high strength, toughness ans structural performance at low weight.

LINCORE® CP PP 20 is a compound reinforced with 30% by mass of flax fibers.

LINCORE® PP FF P2 40 400 is a fabric made of LINCORE® roving (commingled flax and PP filaments). Consolidation is done by heating above melting temperature of PP matrix (180°C-230°C) and applying a low pressure (1-30 bars), before a cooling step under pressure. The molding can be realized by : Diaphragm (1 to 8 bars), Thermo compression (10 to 200 bars), Sandwich thermo compression (1 to 5 bars).

LINCORE® CP ABS 50 is a compound reinforced with 50% by mass of flax fibers.

LINCORE® FF UD 250 is a 100% flax fabric made of untwisted rovings.The molding can be realized by Infusion, Resin Transfer Molding, Resin Film Infusion Lay upThese fabrics are also availble as resin-impregnated reinforcements for high strength, toughness ans structural performance at low weight.

LINCORE® PLA FF P2 40 400 is a fabric made of LINCORE® roving (commingled flax and PLA filaments). Consolidation is done by heating above melting temperature of PLA matric (170°C-200°C) and applying a low pressure (1-30 bars), before a cooling step under pressure.The molding can be realized by diaphragm (1 to 8 bars)- Thermo compression (10 to 200 bars) - Sandwich thermo compression (1 to 5 bars).

LINCORE® CP PLA 30 is a compound reinforced with 30% by mass of flax fibers.

LINCORE® CP PVC 30 is a compound reinforced with 30% by mass of flax fibers.